Dynamic Mechanical Properties of 316L Stainless Steel Fabricated by an Additive Manufacturing Process

Jie Chen,Haiyang Wei,Kuo Bao,Xianfeng Zhang,Yang Cao,Yong Peng,Jian Kong,Kehong Wang
DOI: https://doi.org/10.1016/j.jmrt.2020.12.097
IF: 6.267
2021-01-01
Journal of Materials Research and Technology
Abstract:The cold metal transfer (CMT) process, one of wire and arc additive manufacturing, was utilized to fabricate 316L stainless steel. As-built CMT 316L consists of austenitic coarse columnar grains aligned with depositing direction mainly and tiny areas of scattered ferrite (less than 5%) in dendrite. For comparison purposes, both as-built CMT 316L and annealed wrought 316L were dynamically characterized by Split-Hopkinson Pressure Bar. CMT 316L owns a nearly isotropic characteristic in dynamic compressions. Compared to wrought material, dynamic yield strength and flow stress for the CMT 316L are higher at small strains (below 10%) due to the special cellar structure in matrix but drop lower when the strain was larger than 10% for effect of twinning induced plasticity. Last but not least microstructural characterizations from a series of dynamic compressions of CMT 316L show that average twin thickness reaches maximum at strain rates about 1000–1500 s−1 and followed decreases with the increase of strain rates.
What problem does this paper attempt to address?