Abstract:Laser damage threshold (LDT) is critical for optical devices in high-intensity laser applications. Understanding the influence mechanism of a high-intensity laser on optical materials is principal for improving the materials’ LDTs. Here, the LDT of La 3 Ga 5.5 Nb 0.5 O 14 (LGN) crystals, the most promising nonlinear optical material for mid-infrared optical parametric chirped-pulse amplification (OPCPA), were studied, and its laser damage mechanism was elucidated. Oxygen vacancies in different ligands have important and distinct effects on LDTs and introduce defect levels, playing primary roles in the reduction of LDTs by the absorption of electrons in the conduction bands. The formation of F-centers also decreases LDTs via two-photon absorption. In addition, the linear absorption of free electrons in the conduction bands contributes more than the two-photon absorption, induced by the defect level, in the nanosecond laser damage process. By annealing in optimized conditions, the 0% laser damage probability of the LGN crystals was measured up to 13.1 J/cm 2 , which is a 24% improvement compared with that of the as-grown sample, and the highest of the mid-infrared nonlinear optical crystals. The results can not only lead to further improvements in the laser amplification properties in OPCPA systems but also inspire further studies on the application of optical materials in high-intensity lasers.

Mid-infrared Pulsed Nanosecond Difference Frequency Generation of Oxide LGN Crystal Up to 5.7 Μm.

Few-cycle Pulses Tunable from 3 to 7 Μm Via Intrapulse Difference-Frequency Generation in Oxide LGN Crystals.

Acentric Langanite La_3Ga_55Nb_05O_14 Crystal: a New Nonlinear Crystal for the Generation of Mid-Infrared Parametric Light

Tunable and Coherent Nanosecond 7.2–12.2 Μm Mid-Infrared Generation Based on Difference Frequency Mixing in ZnGeP 2 Crystal

Acentric langanite La<sub>3</sub>Ga<sub>5.5</sub>Nb<sub>0.5</sub>O<sub>14</sub> crystal: a new nonlinear crystal for the generation of mid-infrared parametric light.

Theoretical investigations of broadband mid-infrared optical parametric amplification based on a La<sub>3</sub>Ga<sub>5.5</sub>Nb<sub>0.5</sub>O<sub>14</sub> crystal.

Widely Phase-Matched Tunable Difference-Frequency Generation in Periodically Poled LiNbO3 Crystal

Recent Progress on Acentric La3Nb0.5Ga5.5O14 Crystals: Large-Size Growth and Application to Ultrafast Mid-Infrared Laser Systems [Invited]

High-repetition-rate, Tunable and Coherent Mid-Infrared Source Based on Difference Frequency Generation from a Dual-Wavelength 2 Μm Laser and GaSe Crystal

Theoretical investigations of broadband mid-infrared optical parametric amplification based on a La 3 Ga 5.5 Nb 0.5 O 14 crystal.

Generation of Tunable Coherent Nanosecond 8-12Μm Mid-Infrared Pulses Based on Difference Frequency Generation in GaSe and ZnGeP 2

Nanosecond Optical Parametric Oscillator with Midinfrared Intracavity Difference-Frequency Mixing in Orientation-Patterned GaAs.

Mid-IR difference-frequency generation in OP-GaAs inside the cavity of a narrow-band nanosecond PPLN optical parametric oscillator

Broadband Mid-IR Light Sources From Difference Frequency Generators Based on a 2-mm-Long Aperiodically-Poled Lithium-Niobate Crystal

Difference Frequency Generation Wildly Tunable Continuous Wave Mid-infrared Radiation Laser Source Based on a MgO ∶ PPLN Crystal

6.7-8.1 Μm Tunable Single Frequency Difference Frequency Generation in ZGP for High-Resolution Spectroscopy

Ld End-Pumped 1.11 Mu M Laser of Nd:Ggg Crystal

Laser damage mechanism and threshold improvement of nonlinear optical La₃Ga₅.₅Nb₀.₅O₁₄ crystal for mid-infrared high-intensity laser

Laser Damage Mechanism and Threshold Improvement of Nonlinear Optical La3Ga5.5Nb0.5O14 Crystal for a Mid-Infrared High-Intensity Laser

DFG-based mid-IR tunable source with 0.5 mJ energy and a 30 pm linewidth

Spectral Broadening of a Mixed Nd: CYGA Crystal with Tunable Laser Operation Beyond 1100 Nm.