Facile one-pot synthesis of B-g-C 3 N 4 -Ce (wt%) composite with outstanding pseudocapacitance contribution

Vandana Sairaj,Akshay Sidhi Poovethamkandiyil,Fabeena Jahan Jaleel,Athul Puthiya Purayil,Anjali Paravannoor,Baiju Kizhakkekilikoodayil Vijayan

DOI: https://doi.org/10.1016/j.jre.2024.11.019

IF: 4.632

2024-12-01

Journal of Rare Earths

Abstract:Highlights • A facile one-pot route was followed for the synthesis of B-g-C 3 N 4 -Ce (3%) composite for supercapacitor applications. • An integrated approach of Boron doping and the incorporation of CeO 2 could effectively enhance the specific capacitance of g-C 3 N 4 . • B-g-C 3 N 4 -Ce (3%) single electrodes could deliver a high specific capacitance of 1826.7 F/g at 1.5 A/g. • A capacitive retention of 87% was observed at the end of 10,000 cycles. Rare earth metal oxides possess unique electronic properties, which are highly desirable for the fabrication of pseudocapacitor electrodes. The present study demonstrates the synthesis of boron doped graphitic carbon nitride composite with varying concentrations of cerium (B-g-C 3 N 4 -Ce (wt%)) via a facile one-pot method. A detailed investigation was carried out to elucidate the effects of doping as well as the amount of cerium on the active electrode structure. The structure and morphology of the samples were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). The structural and morphological analysis suggests the incorporation of boron into the graphitic carbon nitride phase, with spherical cerium oxide particles being embedded homogeneously in that matrix. Electrochemical characterization of the samples was carried out using cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) and electrochemical impedance spectroscopy (EIS) and it is found that in-between the potential window of 0–0.45 V in a 3 mol/L potassium hydroxide (KOH) electrolyte, the B-g-C 3 N 4 -Ce (3%) composite displays a superior specific capacitance value of 1826.7 F/g at a current density of 1.5 A/g. The B-g-C 3 N 4 -Ce ( x %) demonstrates excellent pseudocapacitance behavior with a high pseudocapacitance contribution. At current densities of 7.5 A/g, the heterostructure composite B-g-C 3 N 4 -Ce (3%) shows capacitance retention of 87% after 10000 cycles. The synergistic contribution of the individual components of the composite is explained for a better understanding of the capacitive mechanism. Graphical abstract CeO 2 /B-g-C 3 N 4 heterostructure composites (B-g-C 3 N 4 -Ce ( x %)) with various weight percentages of CeO 2 and singly-doped B-incorporated g-C 3 N 4 (B-g-C 3 N 4 ) were prepared and their potential for supercapacitor applications was investigated. Spherical CeO 2 nanoparticles are uniformly embedded to the 2D sheet matrix of B-g-C 3 N 4 . The capacitance property improves due to the enhanced redox activity with the addition of CeO 2 . Download: Download high-res image (315KB) Download: Download full-size image

chemistry, applied