Abstract:Shear experiments were conducted on the cement mortar–sandstone bonding interface and the materials themselves to investigate their loss of shear strength and the deterioration mechanism caused by freezing and thawing cycles. The experimental results show that the shear strength of the bonding interface is much lower than that of the original materials themselves under the same normal stress. The shear strength of this interface decreases linearly with increasing number of freeze–thaw cycles, but it linearly increases with increasing normal stress. The cohesion and internal friction angle also decrease as the number of freeze–thaw cycles increases. In addition, obvious freeze–thaw debonding of this interface is observed and it is first caused by the difference in frost-heaving deformation between the cement mortar and the red sandstone, followed by the frost-heaving pressure in the crack formed in the interface. Finally, the shear damage of this interface has been quantified by reconstitution of the interface morphology. As a result, almost all the shear breakage occurs on the red sandstone side, and a concave rough face arises. With the absence of normal stress, the shear abscission area in the red sandstone increases quickly with increasing number of freeze–thaw cycles. However, with increasing normal stress, this shear abscission area decreases, and the layered composite specimens were prone to shear failure straightly along the bonding interface, because the shear dilatancy deformation is constrained. This study provides the shear failure characteristics of cement mortar–rock interfaces under freeze–thaw cycles and contributes to a better understanding of the freeze–thaw debonding mechanism of protective cement mortar layers on rock surfaces.

Experimental Study on Influence of Cyclic Freeze-Thaw on Shear Strength of Bonding Interface Between Fresh and Old Concrete

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Experimental Study on the Shear Behavior of the Bonding Interface Between Sandstone and Cement Mortar Under Freeze–Thaw

Correlated ATP‐Induced Changes in Membrane Area and Membrane Conductance in Single Rat Adipocytes

Effect of freeze–thaw cycles on the stress–strain curves of unconfined and confined concrete

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Flexural Behaviour of Reinforced Concrete Beams under Freeze–thaw Cycles and Sustained Load

Flexural behaviour of reinforced concrete members subjected to freeze-thaw cycles

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Deterioration of interfacial bonding performance between metal mortar and concrete under the coupling effect of freeze-thaw cycle and abrasion

Experimental study on bond performance of recycled coarse aggregates concrete with circular steel tubes after freeze–thaw cycling

Environmental Factors Influencing The Durability Of Concrete Structures In Frost Environments

Influence of freeze-thaw cycles on the shear performance of silty clay-concrete interface

Experimental Study on Direct Shear Performance of Concrete-Concrete Interface of Prefabricated Structure Sleeve Grouting Connection

Shear Bond Performance at Interface of Concrete-Filled Steel Tube after Freeze-Thaw Cycles

The Influence of Freeze–Thaw Cycles and Corrosion on Reinforced Concrete and the Relationship between the Evolutions of the Microstructure and Mechanical Properties

Influence of Freezing Rate on the Cryo-Deformation and Cryo-Damage of Cement-Based Materials During Freeze-Thaw Cycles

Study on bond properties between near-surface mounted BFRP bars and concrete under freeze-thaw cycles in seawater

Experimental study on compressive strength of concrete with different water content experiencing cryogenic freeze-thaw cycles from room temperature to-190 ℃