Abstract:The rock formations in oil and gas reservoirs are predominantly composed of laminated shale, which contains various defects such as pores and fractures. These defects have a significant impact on the stability of wellbore walls. As a result, this study utilized rock samples from a specific oil and gas reservoir and introduced pre-existing pore and fracture defects within them. Uniaxial compression tests were conducted on rock specimens with varying angles between the fractures and the bedding planes. The study involved measuring and analyzing the impact of pre-existing defect morphology on shale’s mechanical properties. Additionally, through the use of digital image correlation (DIC) technology, a comprehensive strain field map was obtained, depicting the initiation, propagation, and ultimate failure of surface cracks in shale under loading conditions. This allowed for both qualitative and quantitative analysis of the connection between shale’s damage and failure processes and the evolution of strain fields. Ultimately, this research provides a theoretical basis for wellbore stability and the development of shale oil and gas fields. Conclusions drawn from the study are as follows. With an increase in fracture angle, the rock’s elastic modulus gradually increases, and both compressive strength and strain exhibit a pattern of higher values on both ends and lower values in the middle. When the fracture angle is less than 30°, significant stress concentration occurs at the tip of the fracture. When the angle exceeds 60°, stress concentration around pores dominates. In the range of 30° to 60°, there is a combined stress concentration around both pores and fractures, significantly reducing rock stability. Crack propagation is influenced by bedding planes and exhibits varying degrees of ductility, ultimately resulting in a tension-shear mixed failure. When fractures are parallel to bedding planes (angle = 0°), defects are symmetrically distributed, and stress concentration at the fracture tip dominates, leading to crack initiation from the fracture tip and eventually forming an “H”-shaped tensile failure. When fractures are perpendicular to bedding planes (angle = 90°), stress concentration around pores is greater than at the fracture tip, causing cracks to initiate around pores and eventually collapsing on one side of the fracture.

Experimental Study on the Uniaxial Compression Failure and Ultrasonic Transmission of Brittle Shale Considering the Bedding Effect

Experimental Investigation on the Fracture Behaviour of Black Shale by Acoustic Emission Monitoring and CT Image Analysis During Uniaxial Compression

Brittle Failure of Shale under Uniaxial Compression

Study on the Damage and Failure Process of Prefabricated Hole-Fracture Combination Defects in Shale

Cracking Evolution and Failure Characteristics of Longmaxi Shale Under Uniaxial Compression Using Real-Time Computed Tomography Scanning

Study of ultrasonic wave characteristics of shale in triaxial compression tests

Experimental Study on the Failure Mechanisms in Brittle Shales

Investigation on Mechanical Properties, AE Characteristics, and Failure Modes of Longmaxi Formation Shale in Changning, Sichuan Basin, China

Ultrasonic wave propagation characteristics for typical anisotropic failure modes of shale under uniaxial compression and real-time ultrasonic experiments

Experimental and Numerical Investigation of the Effect of Bedding Layer Orientation on Fracture Toughness of Shale Rocks

Behavior of transversely isotropic shale observed in triaxial tests and Brazilian disc tests

Experiment and Discrete Element Modelling on Strength, Deformation and Failure Behaviour of Shale under Brazilian Compression

The investigation on shale mechanical characteristics and brittleness evaluation

Dynamic Mechanical Behavior and Damage Constitutive Model of Shales with Different Bedding under Compressive Impact Loading

An Evaluation Method of Brittleness Characteristics of Shale Based on the Unloading Experiment

Experimental study on crack propagation and failure mode of fissured shale under uniaxial compression

Experiment Study on Damage Properties and Acoustic Emission Characteristics of Layered Shale under Uniaxial Compression

Mechanical Behavior Investigation of Longmaxi Shale under High Temperature and High Confining Pressure

Anisotropic Mechanism and Characteristics of Deformation and Failure of Longmaxi Shale

Experimental investigation on gas permeability in bedding shale with brittle and semi-brittle deformations under triaxial compression

Real-Time Ultrasonic Features and Damage Characterization of Deep Shale