Er3+ and Yb3+ codoped Bi2WO6 upconversion luminescent material preparation and temperature sensing properties
Munire maimaiti,Linxiang Wang,Arepati xiakeer,Mengliang Jiang,Xin Feng,maimaiti, Munire,Wang, Linxiang,xiakeer, Arepati,Jiang, Mengliang,Feng, Xin
DOI: https://doi.org/10.1007/s10854-023-11276-y
2023-10-02
Journal of Materials Science Materials in Electronics
Abstract:Er 3+ and Yb 3+ codoped Bi 2 WO 6 upconversion luminescent materials with different concentrations were prepared via a high-temperature solid-phase method. The microstructure, upconversion luminescence and temperature sensing properties of the synthesized powders were analyzed. From the X-ray diffraction patterns, the doping of Er 3+ and Yb 3+ ions did not affect the orthorhombic crystal structure of the Bi 2 WO 6 matrix material. From the scanning electron microscopy images, the morphologies of the samples were inhomogeneous subspherical particles with a particle size range of 1–5 μm and some agglomeration. SEM-mapping and EDS analysis shows that each element is well distributed in the sample powder particles. At 980 nm excitation, the strongest upconversion emission of Er 3+ was obtained when 1.5% Er 3+ and 0.5% Yb 3+ were codoped, and the four emission peaks of Er 3+ were enhanced with increasing excitation pump power from 50 to 500 mW. The relationship between the excitation pump power and the emission intensity of Er 3+ was determined, and all four emission peaks of Er 3+ were obtained from two-photon absorption. The temperature was characterized by fluorescence intensity ratio of the nonthermally coupled energy levels ( 4 F 9/2 , 4 S 3/2 ) of Er 3+ in the range of 298 K to 573 K, and a maximum absolute temperature sensitivity of 0.0736 K −1 at 573 K and a maximum relative temperature sensitivity of 0.0503 K −1 at 298 K were obtained and were 15.8 and 4.1 times higher than the temperature sensitivity under the thermal coupling energy level ( 2 H 11/2 , 4 S 3/2 ) characterization, respectively. The temperature resolutions under the above thermally coupled and nonthermally coupled energy level pair characterizations were calculated to be 0.07 K and 0.05 K at 333 K, respectively.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied