Conversion of Syngas to Methanol and DME on Highly Selective Pd/ZnAl2O4 Catalyst

Liang Liu,Zenan Lin,Shanya Lin,Yeyun Chen,Lina Zhang,Shaopeng Chen,Xianhua Zhang,Jingdong Lin,Zhaoxia Zhang,Shaolong Wan,Yong Wang

DOI: https://doi.org/10.1016/j.jechem.2020.10.003

IF: 13.1

2021-01-01

Journal of Energy Chemistry

Abstract:Supported Pd catalysts with varied Pd loadings (x = 0.5 wt%, 2.0 wt%, 5.0 wt%, 7.5 wt%, 15.0 wt%) were prepared by the incipient wetness impregnation method using a ZnAl2O4 spinel support. We found that ZnAl2O4 supported Pd catalysts with low Pd loadings (e.g., 0.5 wt%) are very selective in syngas conver-sion to methanol and dimethyl-ether (DME). XRD and TEM characterization shows that, after reduction at 350 degrees C, PdZnis, phase with Pd:Zn molar ratio of 1:1 is favored to form predominantly on the spinel support at relatively low Pd loadings, i.e. less than 5.0 wt%, while Pd-rich PdZna alloy phase exists at Pd loadings above 5.0 wt%. A higher reduction temperature such as 500 degrees C can facilitate the transformation from PdZna to PdZnis, phase in those catalysts with high Pd loading. We further found that catalysts with pre-dominant PdZnis, phase are selective in the methanol and DME production from syngas, while the pres-ence of PdZna phase leads to the notable formation of alkanes byproducts, resulting in reduced methanol and DME selectivity. DME formation from dehydration of methanol depends on the acidity of catalysts, which was found to increase with Pd loading, probably due to the formation of isolated Al2O3 as a result of Zn migrating from ZnAl2O4 spinel phase to form the PdZn phases with Pd. (C) 2020 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by ELSEVIER B.V. and Science Press. All rights reserved.