Damage Evolution During the Dynamic Tensile Fracture(spallation)of Metallic Glasses
Xiaochang Tang,Lingyi Meng,Xiaohu Yao
DOI: https://doi.org/10.1360/tb-2020-0995
2020-01-01
Chinese Science Bulletin (Chinese Version)
Abstract:Metallic glasses (BMGs) possess many excellent mechanical and physical properties thanks to their unique amorphous structures, and have potential applications in the field of armor protection. Pioneering works have established some fundamental understandings of their mechanical responses, including the extremely large Hugoniot elastic limit and the possible phase transition captured by some equation of state. But other essential factors dominate the material selection for applications involving high strain rate loading. Our focus here is the dynamic tensile fracture induced by severe stress wave interaction following the passage of a shock compression pulse, known as spall fracture or spallation. This failure process is of great interest to engineering and defense applications such as satellite shielding and armor materials, especially for materials of relatively low tensile strength such as BMGs. To meet the needs of this kind of application, it is necessary to deepen the understanding of its dynamic mechanical properties and damage evolution process. Previous reviews on metallic glasses generally focus on their physical properties, atomic structures, shear band evolutions under relatively low strain rates, and dynamic fracture at high strain rate loading. On the other hand, reviews on dynamic tensile fracture (spallation) only involves traditional materials such as crystals and polymers. Currently, there is no review on the spall damage evolution of metallic glasses, which is the basic topic of this work. In this paper, the researches of dynamic mechanical properties and spall damage evolution mechanisms of metallic glasses are introduced in detail, as well as the shortcomings of existing experimental work and theoretical models. In recent years, a "ductile-brittle transition" phenomenon observed on the spallation surface of metallic glasses may accelerate the dynamic damage evolution process of materials and affect its practical applications in national defense, military, and aerospace. At a relatively lower impact velocity, spallation occurs in the form of a flat plane surrounded by sporadic micro-voids. Rough fracture morphology consists of dimples (post-mortem signatures of coalesced voids) that dominate the spall fracture morphology. At higher impact velocities, this becomes a smoother fracture surface induced by conical shear bands, termed as "cup-cone" structures. Such a transition represents a "ductile-brittle transition" and appears to be a fundamental spallation mechanism in BMGs. Aiming at understanding the spallation process of BMGs, especially in the form of growing microvoids, we also provide a brief review of void growth theories. The roles of strain hardening, viscosity, and inertia dominate spall strength at low, intermediate, and extremely high strain rates, respectively. Moreover, the early stage of void growth was observed to be mainly controlled by viscosity, but inertia was predicted to dominate the long term void growth process. Both viscosity and inertia were shown to improve the spall strength and reduce the void growth rate during dynamic loading when compared with the rate-independent counterpart. From the microscopic scale, the dynamic yields stress and flow stress of the solid material surrounding a void increases with viscosity and strain hardening, resulting in a reduction in the void growth rate. The role of strain hardening would be further enhanced with a larger strain gradient, especially for sub-micron scale voids. For planar impact situations, an increase in spall nucleation site density with increasing impact pressure was suggested, since smaller voids may not be sufficiently activated at low pressure. On the other hand, thermal softening reversely accelerates void growth at the later stage by reducing the yield stress, which has little influence on spall strength. The reason is that the spall strength is determined during the early stage of void growth, in which temperature rise has been quickly dissipated by heat conduction.