Abstract:Fracture in aluminum alloys with precipitates involves at least two mechanisms, namely, ductile fracture of the aluminum-rich matrix and brittle fracture of the precipitates. In this work, a coupled crystal plasticity-phase field model for mixed ductile-brittle failure modes is formulated and used to investigate the effect of precipitate morphology and size distribution on damage evolution in aluminum alloys. A thermodynamically consistent framework for elastic and plastic work dissipation in the fracture process zone is used to formulate the coupled constitutive behavior for brittle and ductile damage, respectively. Representative Volume Elements (RVE) with varying particle morphology and orientation were generated and their uni-axial loading was simulated to assess the damage resistance of the different model microstructures. For critical energy release rate $G_c$ values of the aluminum matrix ranging from 4 to 8~Jm$^{-2}$ for single crystals and from 10 to 16~Jm$^{-2}$ for polycrystals, the model predicts a change in failure modes from particle debonding to cracking followed by ductile matrix failure. The change of particle failure mechanism as a result of increased $G_c$ is observed for both, single and polycrystalline model microstructures. For the case of particle debonding, microstructures with circular or ellipsoidal particles (with the major axis perpendicular to the loading direction) show a higher ductility and fracture work compared to the other studied cases. In the case of particle cracking, microstructures with ellipsoidal particles aligned parallel to the loading axis show a higher ductility and fracture work among the investigated cases. The simulations qualitatively reproduce the experimentally observed particle failure mechanisms (cracking and debonding) for two different matrix alloy classes (commercially pure and 2xxx alloys) reinforced with ceramic particles.

Gradient-enhanced crystal plasticity coupled with phase-field fracture modeling

Phase-field modeling of ductile fracture across grain boundaries in polycrystals

A Gradient-Enhanced Plasticity Based Phase-Field Model for Ductile Fracture Simulations

Anisotropic Damage Model under Continuum Slip Crystal Plasticity Theory for Single Crystals

A mechanism-based gradient damage model for metallic fracture

A novel micromechanics-enhanced phase-field model for frictional damage and fracture of quasi-brittle geomaterials

Modeling of inter- and transgranular stress corrosion crack propagation in polycrystalline material by using phase field method

Phase-Field Modeling of Coupled Brittle-Ductile Fracture in Aluminum Alloys

Phase field modelling of crack propagation in functionally graded materials

A comparative study between phase‐field and micromorphic gradient‐extended damage models for brittle fracture

Modelling of Micro-Plasticity Evolution in Crystalline Materials

Crystal Plasticity Finite Element Model Based on Dislocation Density Evolution Coupling with Thermal Activation and Damage Mechanism

Phase-field, dislocation based plasticity and damage coupled model: Modelling and application to single crystal superalloys

A micromechanics-based variational phase-field model for fracture in geomaterials with brittle-tensile and compressive-ductile behavior

Crack phase-field model equipped with plastic driving force and degrading fracture toughness for ductile fracture simulation

A phase field model for deformation-induced amorphization

A Variational Phase-Field Model For Ductile Fracture with Coalescence Dissipation

A ductile phase-field model based on degrading the fracture toughness: Theory and implementation at small strain

Coupling of a Phase-Field Method with a Nonlocal Micro-Mechanical Damage Model for Simulating Ductile Fracture

A duality‐based coupling of Cosserat crystal plasticity and phase field theories for modeling grain refinement

Phase Field Coupled Finite Deformation Plasticity Formulation of Ductile Fracture With Nonlinear Kinematic Hardening and Modified Energy Release Function