Abstract:The excellent properties including high porosity, large specific surface area, low density, and strong controllability of metal-organic frameworks (MOFs) make them one of the preferred materials for a plethora of applications. One particular intriguing application, among others, is microwave absorption, to which majority of research has been devoted by using MOF as templates to prepare porous carbon via carbonization. Contrary to such approach, in this study we propose a novel strategy based on leveraging the intrinsic attributes of MOF. Through a simple and rapid microwave solvothermal method, lamellar redox-active iron-quinoid MOFs were synthesized and their morphology and crystallinity are modulated as a function of reaction temperature. The conductivity of the prepared MOF reached up to 2 x 10(-3) S/m, which is comparable to that of semiconductors. In addition, magnetic hysteresis was observed at 300 K. The reaction temperature proved pivotal to attain maximum microwave absorption of -73.5 dB at 13.8 GHz with a matching thickness of 3.3 mm. Effective absorbing bandwidth with a reflection loss below -10 dB can be also gained in a wide frequency range of 9.8-15.9 GHz. The optimal microwave absorbing performance was mainly attributed to the simultaneous implementation of magnetic and electrical loss in a single iron-quinoid MOF resulting in adequate impedance matching through modulable magnetic and electric properties. The developed iron-quinoid MOF material opens up new opportunities to achieve high-efficiency, lightweight and tunable microwave absorbers. The material-structure coupling strategy here is instrumental to developing next-generation high-performance microwave absorbing materials.

Low Weight Hollow Microspheres of Iron with Thin Dielectric Coating: Synthesis and Microwave Permeability

Electromagnetic and Microwave Absorption Properties of Carbonyl Iron/Mno2 Composite

Facile Synthesis of Porous Coin-Like Iron and Its Excellent Electromagnetic Absorption Performance

Synthesis of Hollow Carbonyl Iron Microspheres Via Pitting Corrosion Method and Their Microwave Absorption Properties

Ultrafine FeCo Nanoparticles Isolated by Ultrathin Dielectric Shells for Microwave Application

A MOF-driven porous iron with high dielectric loss and excellent microwave absorption properties

Dielectric enhancement effect in biomorphic porous carbon-based iron@iron carbide ‘meta-powder’ for light-weight microwave absorption material design

Microwave Absorption Performance of 2D Iron-Quinoid MOF

The microwave electromagnetic and absorption properties of some porous iron powders

Ferromagnetic Co20Ni80 Nanoparticles Encapsulated Inside Reduced Graphene Oxide Layers with Superior Microwave Absorption Performance

Dielectric and electrical studies on iron oxide (α-Fe2O3) nanoparticles synthesized by modified solution combustion reaction for microwave applications

Influence of Weight Ratio of Ball-to-Powder on Flake-Shaped Process and Electromagnetic Properties of Carbonyl Iron Powders

Synthesis of yolk-shell structured carbonyl iron@void@nitrogen doped carbon for enhanced microwave absorption performance

Synthesis of Iron-Based Hexagonal Microflakes for Strong Microwave Attenuation

Synthesis, Structure and Dynamic Magnetic Properties of Double-Layered Ni-Fe1−xCoxhollow Microspheres

Heterogeneous iron-nickel compound/RGO composites with tunable microwave absorption frequency and ultralow filler loading.

Synthesis, Dielectric, and Microwave Absorption Properties of Flake Carbonyl Iron Particles Coated with Nanostructure Polymer

Excellent microwave absorption performances of high length-diameter ratio iron nanowires with low filling ratio

Heterogeneous iron-nickel compound/RGO composites with tunable microwave absorption frequency and ultralow filler loading

Construction of Iron Oxide@C@Fe Heterointerfaces by Oxygen Atmosphere Heat Treatment for Enhanced Microwave Absorption Performance

Porous and flake-like γ′-Fe4N@iron oxides with enhanced microwave absorption performance