Superparamagnetic nanocubes of Co and Cu co-doped Mn-based ferrites as microwave absorbing material
Parveen Kumar,Praveen Negi,Alok K. Dixit,Himangshu Bhusan Baskey,Sumit Kumar,Ashish Kumar Mishra,Ashavani Kumar
DOI: https://doi.org/10.1016/j.matchemphys.2024.129360
IF: 4.778
2024-04-28
Materials Chemistry and Physics
Abstract:The requirement in resolving electromagnetic (EM) problems in stealth warhead technologies are excellent absorption ability, lightweight, and thin dimensions. In this direction, this study provides a straightforward hydrothermal one-pot method to synthesize superparamagnetic Mn-based ferrite co-doped with Co and Cu (MCCF), and the article presents its microwave absorption properties. Using cutting-edge techniques, the MCCF nanocomposite phase structure, morphological, superparamagnetic, and microwave absorption properties were measured and analyzed. MCCF-822 ferrite shows superparamagnetic properties simultaneously with a high M s value 71.4 emu/g. Vector network analysis of MCCF-822 with 70 wt% loading demonstrates an effective absorption bandwidth (EAB) of 5.2 GHz with a maximum reflection loss (RL max ) of −19.2 dB at 2 mm thickness, and it spans almost 92.77 % frequency region (3.3–18 GHz range with RL < −10 dB) by varying thickness 1.7 mm–6 mm. At 60 wt% loading, it covers the whole X & K u band with a thickness range from 2 to 9 mm with a good EAB of 4.3 GHz at 2.5 mm thickness with RL max of −16 dB. The dual absorption bands are also present in MCCF-613, which increases the EAB with RL max −52.99 dB at 9 mm, fulfilling the superparamagnetic properties. Thus, MCCF-822 is proposed as a cost-effective superior ferrite nanocomposite for microwave absorption applications.
materials science, multidisciplinary