Phase Compatible NiFe 2 O 4 Coating Tunes Oxygen Redox in Li-Rich Layered Oxide
Jiming Peng,Yu Li,Zhiqiang Chen,Gemeng Liang,Sijiang Hu,Tengfei Zhou,Fenghua Zheng,Qichang Pan,Hongqiang Wang,Qingyu Li,Jianwen Liu,Zaiping Guo
DOI: https://doi.org/10.1021/acsnano.1c02023
IF: 17.1
2021-06-24
ACS Nano
Abstract:Li-rich layered oxides have attracted intense attention for lithium-ion batteries, as provide substantial capacity from transition metal cation redox simultaneous with reversible oxygen-anion redox. However, unregulated irreversible oxygen-anion redox leads to critical issues such as voltage fade and oxygen release. Here, we report a feasible NiFe<sub>2</sub>O<sub>4</sub> (NFO) surface-coating strategy to turn the nonbonding coordination of surface oxygen into metal–oxygen decoordination. In particular, the surface simplex M–O (M = Ni, Co, Mn from MO<sub>6</sub> octahedra) and N–O (N = Ni, Fe from NO<sub>6</sub> octahedra) bonds are reconstructed in the form of M–O–N bonds. By applying both <i>in operando</i> and <i>ex situ</i> technologies, we found this heterostructural interface traps surface lattice oxygen, as well as restrains cation migration in Li-rich layered oxide during electrochemical cycling. Therefore, surface lattice oxygen behavior is significantly sustained. More interestingly, we directly observe the surface oxygen redox decouple with cation migration. In addition, the NFO-coating blocks HF produced from electrolyte decomposition, resulting in reducing the dissolution of Mn. With this strategy, higher cycle stability (91.8% at 1 C after 200 cycles) and higher rate capability (109.4 mA g<sup>–1</sup> at 1 C) were achieved in this work, compared with pristine Li-rich layered oxide. Our work offers potential for designing electrode materials utilizing oxygen redox chemistry.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02023?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02023</a>.Estimated costs of several coating materials; chemical compositions; ICP-AES results; XRD patterns; crystallographic data and structures; Raman spectra; SEM and TEM images; XPS spectra; STEM-EDS elemental mapping; electrochemical performance of NFO-coated LNCM; electrochemical performance comparison; average charge and discharge voltage, voltage vs specific capacity profiles, and <i>Q</i>/d<i>V</i> curves of LNCM and NFO3; XRD pattern and voltage profile of pure NFO; electrochemical performance of LNCM and NFO3 electrode at 55 °C; GC profiles of gas components collected from LNCM and NFO3 electrodes; excerpts from Raman spectra of LNCM and NFO3; <i>ex situ</i> XRD patterns (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02023/suppl_file/nn1c02023_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology