Abstract:In this paper, 2 atom % Al-doped ZnO (AZO) was prepared by the co-precipitation method together with sparking plasma sintering (SPS) treatment. The as-synthesized AZO powders show the morphology of hollow hexagonal towers, which result in a high porosity of 50.6% in the bulk sample consolidated by SPS sintering at 400 °C, and the porosity decreases gradually with increasing sintering temperature up to 1000 °C. Positron annihilation measurements reveal that even after sintering at 1000 °C, there are still a considerable number of small pores. A high electrical conductivity of 3 × 105 S m–1 is achieved at room temperature for the AZO sample sintered at 1000 °C, while the absolute values of Seebeck coefficient keep at relatively high values between 59 and 144 μV K–1 in the measurement temperature range of 27–500 °C, leading to a high power factor of 3.4 × 10–3 W m–1 K–2. On the other hand, the pores in AZO act as strong phonon scattering centers, and an extremely low thermal conductivity of 1.5 W m–1 K–1 measured at room temperature is obtained for AZO sintered at 400 °C. Due to the residual pores in the 1000 °C-sintered sample, the thermal conductivity is still relatively low. As a result, a maximum ZT of 0.275 measured at 500 °C is obtained in this sample, which is the highest ZT reported for ZnO around this temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16506?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16506</a>.Thermal gravity analysis for the Al-doped ZnO (Figure S1), TEM images of Al-doped ZnO sintered at different temperatures (Figure S2), and structural characterization and thermoelectric properties of undoped ZnO prepared by co-precipitation combined with SPS treatment (Figures S3–S5) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16506/suppl_file/am0c16506_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Infrared Emission Characteristic and Microwave Loss Property of Aluminum Doped Zinc Oxide Nanoparticles

Surface Topography and Optical Properties of Al-doped ZnO Thin Films by Sol-gel Process

Study on Aluminum Concentration on Optical and Electrical Properties of AZO Thin Films Fabricated by Ultrasonic Spray Pyrolysis

Preparation and Properties of Aluminum-Doped Zinc Oxide Ultrafine Powders

Aluminum-doped zinc oxide nanoparticles with tunable near-infrared absorption/reflectance by a simple solvothermal process

Optical Properties of Al-Doped ZnO Films in the Infrared Region and Their Absorption Applications

Ultrafast Carrier Dynamics and Third Order Nonlinear Optical Properties of Aluminum Doped Zinc Oxide (AZO) Thin Films

Microstructure and Electrical Properties of Al-doped ZnO Thin Films

Significant Enhancement in the Thermoelectric Performance of Aluminum-Doped ZnO Tuned by Pore Structure

Influence of Al Doping on the Properties of Zno Thin Films Grown by Atomic Layer Deposition

Preparation And Properties For Aluminum-Doped Zinc Oxide Powders With The Coprecipitation Method

Micrographs and Optical Properties of Al-Doped Zno Thin Films Deposited by Radio Frequency Magnetron Sputtering

Effects of Al doping on the optical and electrical properties of pre-synthesized ZnO powders by solid state method

Optical and structural properties of Al-ZnO nanocomposites

Versatile r.f. magnetron sputtering doping method to produce aluminum‐doped zinc oxide films

Effect of the annealing temperature on the refractive index and extinction coefficient of aluminum-doped zinc oxide: a low-cost electron transport layer

Infrared Properties And Mechanism Of Al-Doped Zno Thin Films

High Dielectric Constant in Al-doped ZnO Ceramics Using High-Pressure Treated Powders

Property Research of ZnO:Al Thin Films with Different Proportion of Al3+ Doping

Preparation and Characterization of Aluminum Doped ZnO

Microstructure and optical properties of ZnAlO films prepared by Magnetron sputtering