Abstract:To afford an intact double network (sample abbr.: DN) hydrogel, two-step crosslinking reactions of poly(2-acrylamido-2-methylpropanesulfonic acid) (i.e., PAMPS first network) and then poly(acrylic acid) (i.e., PAA second network) were conducted both in the presence of crosslinker (N,N′-methylenebisacrylamide (MBAA)). Similar to the two-step processes, different contents of 2,2,6,6-tetramethyl-1-piperidinyloxy (TEMPO) oxidized cellulose nanofibers (TOCN: 1, 2, and 3 wt.%) were initially dispersed in the first network solutions and then crosslinked. The TOCN-containing PAMPS first networks subsequently soaked in AA and crosslinker and conducted the second network crosslinking reactions (TOCN was then abbreviated as T for DN samples). As the third step, various (T–)DN hydrogels were then treated with different concentrations of FeCl3(aq) solutions (5, 50, 100, and 200 mM). Through incorporations of ferric ions into (T–)DN hydrogels, notably, three purposes are targeted: (i) strengthen the (T–)DN hydrogels through ionic bonding, (ii) significantly render ionic conductivity of hydrogels, and (iii) serve as a catalyst for the forth step to proceed with in situ chemical oxidative polymerizations of pyrroles to afford polypyrrole-containing (sample abbr.: Py) hydrogels [i.e., (T–)Py–DN samples]. The characteristic functional groups of PAMPS, PAA, and Py were confirmed by FT–IR. Uniform microstructures were observed by cryo scanning electron microscopy (cryo-SEM). These results indicated that homogeneous composites of T–Py–DN hydrogels were obtained through the four-step process. All dry samples showed similar thermal degradation behaviors from the thermogravimetric analysis (TGA). The T2–Py5–DN sample (i.e., containing 2 wt.% TOCN with 5 mM FeCl3(aq) treatment) showed the best tensile strength and strain at breaking properties (i.e., σTb = 450 kPa and εTb = 106%). With the same compositions, a high conductivity of 3.34 × 10−3 S/cm was acquired. The tough T2–Py5–DN hydrogel displayed good conductive reversibility during several “stretching-and-releasing” cycles of 50–100–0%, demonstrating a promising candidate for bioelectronic or biomaterial applications.

Preparation of Novel Temperature-Responsive Double-Network Hydrogel Reinforced with Aramid Nanofibers

Dual Ionically Cross-linked Double-Network Hydrogels with High Strength, Toughness, Swelling Resistance, and Improved 3D Printing Processability

Preparation and Characterization of Ph- and Temperature-Responsive Nanocomposite Double Network Hydrogels.

Interpenetrating Thermophobic and Thermophilic Dual Responsive Networks

Fabrication of Thermo-Responsive Controllable Shape-Changing Hydrogel

Tough Supramolecular Hydrogels with Excellent Self-Recovery Behavior Mediated by Metal-Coordination Interaction

Preparation and Characterization of Dual-Sensitive Double Network Hydrogels with Clay As a Physical Crosslinker

Phase Transition Temperature Controllable Poly(acrylamide- Co -Acrylic Acid) Nanocomposite Physical Hydrogels with High Strength

The preparation of double network hydrogel with high mechanical properties by photopolymerization under the green LED irradiation and enhancement of wet adhesion by tannic acid

Preparations of Tough and Conductive PAMPS/PAA Double Network Hydrogels Containing Cellulose Nanofibers and Polypyrroles

A mechanically robust double-network hydrogel with high thermal responses via doping hydroxylated boron nitride nanosheets

Fabrication of Double-Network Hydrogels with Universal Adhesion and Superior Extensibility and Cytocompatibility by One-Pot Method

Preparation and Properties of Double Network Hydrogel with High Compressive Strength

High-Strength, Tough, Fatigue Resistant, and Self-Healing Hydrogel Based on Dual Physically Cross-Linked Network

Highly swelling, tough intelligent self-healing hydrogel with body temperature-response

Strong, tough, fatigue-resistant and 3D-printable hydrogel composites reinforced by aramid nanofibers

Double physical network hydrogels with rapid self-recovery and multistimuli-responsive shape memory effects based on low-methoxyl pectin and host-guest interactions

High Performance Soft Fiber-Reinforced Sodium Alginate/Polyacrylamide Double-Network Hydrogels

Spider silk inspired strong yet tough composite hydrogels

A novel dual responsive nanocomposite double network hydrogel with good mechanical property

Properties and toughening mechanisms of PVA/PAM double-network hydrogels prepared by freeze-thawing and anneal-swelling