Abstract:To afford an intact double network (sample abbr.: DN) hydrogel, two-step crosslinking reactions of poly(2-acrylamido-2-methylpropanesulfonic acid) (i.e., PAMPS first network) and then poly(acrylic acid) (i.e., PAA second network) were conducted both in the presence of crosslinker (N,N′-methylenebisacrylamide (MBAA)). Similar to the two-step processes, different contents of 2,2,6,6-tetramethyl-1-piperidinyloxy (TEMPO) oxidized cellulose nanofibers (TOCN: 1, 2, and 3 wt.%) were initially dispersed in the first network solutions and then crosslinked. The TOCN-containing PAMPS first networks subsequently soaked in AA and crosslinker and conducted the second network crosslinking reactions (TOCN was then abbreviated as T for DN samples). As the third step, various (T–)DN hydrogels were then treated with different concentrations of FeCl3(aq) solutions (5, 50, 100, and 200 mM). Through incorporations of ferric ions into (T–)DN hydrogels, notably, three purposes are targeted: (i) strengthen the (T–)DN hydrogels through ionic bonding, (ii) significantly render ionic conductivity of hydrogels, and (iii) serve as a catalyst for the forth step to proceed with in situ chemical oxidative polymerizations of pyrroles to afford polypyrrole-containing (sample abbr.: Py) hydrogels [i.e., (T–)Py–DN samples]. The characteristic functional groups of PAMPS, PAA, and Py were confirmed by FT–IR. Uniform microstructures were observed by cryo scanning electron microscopy (cryo-SEM). These results indicated that homogeneous composites of T–Py–DN hydrogels were obtained through the four-step process. All dry samples showed similar thermal degradation behaviors from the thermogravimetric analysis (TGA). The T2–Py5–DN sample (i.e., containing 2 wt.% TOCN with 5 mM FeCl3(aq) treatment) showed the best tensile strength and strain at breaking properties (i.e., σTb = 450 kPa and εTb = 106%). With the same compositions, a high conductivity of 3.34 × 10−3 S/cm was acquired. The tough T2–Py5–DN hydrogel displayed good conductive reversibility during several “stretching-and-releasing” cycles of 50–100–0%, demonstrating a promising candidate for bioelectronic or biomaterial applications.

Preparation and Characterization of Dual-Sensitive Double Network Hydrogels with Clay As a Physical Crosslinker

Macroporous double-network cryogels: Formation mechanism, enhanced mechanical strength and temperature/pH dual sensitivity

Preparation and Characterization of Ph- and Temperature-Responsive Nanocomposite Double Network Hydrogels.

Study on A New Polymer/Graphene Oxide/Clay Double Network Hydrogel with Improved Response Rate and Mechanical Properties

Synthesis and Properties of a Novel Double Network Nanocomposite Hydrogel

Synthesis and Characterization of Ph and Temperature Double-Sensitive Nanocomposite Hydrogels Consisting of Poly(Dimethylaminoethyl Methacrylate) and Clay

Interpenetrating Thermophobic and Thermophilic Dual Responsive Networks

Relationship between crosslinking structure and tensile properties of a double network nano-composite hydrogel

pH/temperature double responsive behaviors and mechanical strength of laponite‐crosslinked poly(DEA‐co‐DMAEMA) nanocomposite hydrogels

Study of double network hydrogels based on sodium methacrylate alginate and carboxymethyl chitosan

Preparation and Characterization of Acid Resistant Double Cross-Linked Hydrogel for Potential Biomedical Applications.

Synthesis and Characterization of Partially Biodegradable and Thermosensitive Hydrogel

Preparation and characterization of double macromolecular network (DMMN) hydrogels based on hyaluronan and high molecular weight poly(ethylene glycol)

Synthesis and mechanical strength of a novel double network nanocomposite hydrogel with core-shell structure

Preparation of Novel Temperature-Responsive Double-Network Hydrogel Reinforced with Aramid Nanofibers

Novel Interpenetrating Networks (Ipns) Hydrogels Prepared In Situ By Liquid-Phase Photopolymerization

Preparation and Characterization of Hybrid Double Network Chitosan/poly(acrylic Amide-Acrylic Acid) High Toughness Hydrogel Through Al3+ Crosslinking.

Double-network hydrogels for biomaterials: Structure-property relationships and drug delivery

Dual cross-linked networks hydrogels with unique swelling behavior and high mechanical strength: Based on silica nanoparticle and hydrophobic association

Stereocomplexation of Poly(lactic acid) and Chemical Crosslinking of Ethylene Glycol Dimethacrylate (EGDMA) Double-Crosslinked Temperature/pH Dual Responsive Hydrogels

Preparations of Tough and Conductive PAMPS/PAA Double Network Hydrogels Containing Cellulose Nanofibers and Polypyrroles