Abstract:Hydrogels have demonstrated significant potential in wound dressings, owing to their adjustable water content, excellent biocompatibility, and other advantages. An ideal wound dressing requires absorbing exudate while maintaining mechanical properties to prevent secondary damage to the wound under external pressure. In this study, Polyacrylic Acid (PAA)/Chitosan (CS) double network hydrogels were prepared via radical polymerization, and the swelling ratio, compressive modulus, and other parameters were experimentally measured. A hyperelastic finite element model of the hydrogel was then established, and its rationality was validated by experiments. Based on the model, the impacts of CS content and dynamic water content on the compressive properties of PAA/CS hydrogels were analyzed. Tetracycline hydrochloride was loaded into PAA/CS hydrogels, the drug release performance and adhesion experiments were carried out. The results indicated that, compared with the hydrogels with 2.5% and 5% CS content, the hydrogel with 1% CS content had the highest swelling ratio, which was 1774%. Meanwhile, its equilibrium water content could attain 94.6%. When the water content varied within the range from 45% to 75%, the compressive strength of the hydrogel with 5% CS content ranged from 0.33 MPa to 1.22 MPa, similar to that of skin tissue. Additionally, the prepared drug-loaded PAA/CS hydrogels exhibited a drug release pattern approximately following the Korsmeyer-Peppas model within 7 days. They also exhibited remarkable adhesion to porcine skin and different substrate surfaces. This study provides a basis for the clinical application of PAA/CS double network hydrogels as wound dressings in the repair of infected wounds.

Study of double network hydrogels based on sodium methacrylate alginate and carboxymethyl chitosan

Dual Ionically Cross-linked Double-Network Hydrogels with High Strength, Toughness, Swelling Resistance, and Improved 3D Printing Processability

Double-network hydrogels for biomaterials: Structure-property relationships and drug delivery

Chitosan‐based Double Network Hydrogels with Self‐healing and Dual‐responsive Shape Memory Abilities

Interpenetrating Polymer Network Hydrogels Composed of Chitosan and Photocrosslinkable Gelatin with Enhanced Mechanical Properties for Tissue Engineering

Polyacrylamide/Copper-Alginate Double Network Hydrogel Electrolyte with Excellent Mechanical Properties and Strain-Sensitivity

Double crosslinking hydrogel with tunable properties for potential biomedical application

Double network hydrogels from polyzwitterions: high mechanical strength and excellent anti-biofouling properties

Preparation and Characterization of Dual-Sensitive Double Network Hydrogels with Clay As a Physical Crosslinker

Construction of polysaccharide based physically crosslinked double-network antibacterial hydrogel

Fabrication and Characterization of One Interpenetrating Network Hydrogel Based on Sodium Alginate and Polyvinyl Alcohol

Dual Physically Cross-Linked κ-Carrageenan-Based Double Network Hydrogels with Superior Self-Healing Performance for Biomedical Application

High Performance Soft Fiber-Reinforced Sodium Alginate/Polyacrylamide Double-Network Hydrogels

Study on A New Polymer/Graphene Oxide/Clay Double Network Hydrogel with Improved Response Rate and Mechanical Properties

Study on the mechanical properties of Polyacrylic Acid/Chitosan double network hydrogels in dynamic water content

Preparation and characterization of multi-network hydrogels based on sodium alginate/krill protein/polyacrylamide—Strength, shape memory, conductivity and biocompatibility

The preparation of double network hydrogel with high mechanical properties by photopolymerization under the green LED irradiation and enhancement of wet adhesion by tannic acid

Carboxymethyl chitosan/polyacrylamide double network hydrogels based on hydrogen bond cross-linking as potential wound dressings for skin repair

Janus Nanoparticle Coupled Double‐Network Hydrogel

Injectable Networks Based on a Hybrid Synthetic/Natural Polymer Gel and Self-Assembling Peptides Functioning as Reinforcing Fillers