Abstract:Aligned poly(vinyl alcohol) (PVA) fibers with diameters of about 180 ± 22 nm were obtained by using a wire–drum collector during electrospinning of aqueous solutions of PVA with 99% hydrolysis. The fiber orientation factor, defined by the Herman’s orientation function, was about 0.95 with respect to the collecting direction. Subjected to a stepwise heating protocol, the crystal orientation and crystallinity in the aligned fibers at different annealing temperatures (T a) were determined by using Fourier transform infrared spectroscopy (FTIR) and synchrotron 2D wide-angle X-ray diffraction (WAXD). Upon heating, FTIR results disclosed the desorption of residual water molecules at T a < 100 °C and an increase in crystal orientation at elevated temperatures as-revealed by the decreasing dichroism of the crystal-related band at 1143 cm–1 until fiber melting, followed by thermal degradation at T a ≳ 190 °C. The enhanced crystal orientation along the fiber axis at high T a (≳100 °C) was also validated by the detailed analyses of the 2D WAXD patterns to extract the Herman’s orientation factor of the reciprocal lattice vectors of the (101/101̅) crystal planes from which the chain orientation factor in the crystalline phase was derived to dramatically increase from 0.57 at 35 °C to reach the highest value of 0.88 at 200 °C. Meanwhile, the fiber crystallinity was also increased upon heating from 31% at 35 °C to 35% at 100 °C and further up to 37% at 180 °C. The peculiar two-step enhancement in the crystal orientation and fiber crystallinity at elevated temperatures is attributed to the presence of the fibrils comprising the fiber, which are composed of highly oriented amorphous chains as well as the loosely packed amorphous chains existing in between the oriented crystalline domains. The presence of fibrils and fiber bundles (superstructures of the fibrils) was validated by atomic force microscopy as well as scanning and transmission electron microscopy. The highly oriented amorphous chains were disclosed by the anomalous meridional X-ray diffraction with a unique spacing of 2.44 Å, which is associated with the spacing along the chain axis in the closely packed and aligned chains with zigzag conformation. These extended amorphous chains may form strong intrachain and interchain hydrogen bonds, which firmly hold the fiber integrity for restricting orientation relaxation of chain molecules upon heating, therefore, to readily proceed the chain reorganization and develop oriented crystals directly at high T a. The unique features of fibrils existing in the as-spun PVA fibers are relevant to the flow-induced phase separation of the electrospinning jet to produce phase-separated structure of strings with various widths. A discussion on the structures evolved from the liquid strings to the solid fibrils and subsequent heating effect is provided.

Melting Temperature of Individual Electrospun Poly(vinylidene Fluoride) Fibers Studied by AFM-based Local Thermal Analysis

A Study on the Relationship Between the Crystal Structure and Hard Elasticity of PVDF Fibers

Comprehensive Characterization of PVDF Nanofibers at Macro- and Nanolevel

Changes In Crystalline Structures Of Electrospinning Solutions Of Pvdf During Thermal Treatment

Poly(vinyl alcohol) Fibrils with Highly Oriented Amorphous Chains Developed in Electrospun Nanofibers

Crystalline Structure Changes of Poly(vinylidene fluoride) Fibers during Stretching Process

Mechanical Properties of Magnetic-Field-Assisted Electrospun Poly(vinylidene Fluoride) (PVDF) Nanofibers.

Influence of Solution Parameters on Phase Formation and Morphology of Electrospun Poly(vinylidene fluoride) Nanofiber

Controlling the surface structure, mechanical properties, crystallinity, and piezoelectric properties of electrospun PVDF nanofibers by maneuvering molecular weight

Structures And Properties Of Wet Spun Thermo-Regulated Polyacrylonitrite-Vinylidene Chloride Fibers

Fabrication and Characterization of Electrospun Poly(acrylonitrile-co-vinylidene Chloride) Copolymer/Poly(n-tetradecyl Acrylate-Co-n-hexadecyl Acrylate) Sheath/Core Nanofiber-wrapped Thermo-regulated Filaments

Control of diameter and morphology of poly(vinylidene fluoride) nanofibers fabricated by electrospinning

Thermal Conductivity of Individual Electrospun Polymer Nanofibers

Effect of MMT, SiO2, CaCO3, and PTFE nanoparticles on the morphology and crystallization of poly(vinylidene fluoride)

Rheological Properties of Poly(Vinylidene Fluoride) in Molten State

Fabrication of Poly(vinylidenefluoride‐co‐hexafluoropropylene) Nanofiber Yarns by Conjugate Electrospinning

Predicting Polymorphism of Electrospun Polyvinylidene Fluoride Membranes by Their Morphologies

Exploration of Melt-Electrospinning Based on the Novel Device

Detailed Analysis of Temperature Dependences of Spherulite Morphology and Crystallite Orientation of Poly(Vinylidene Fluoride) Via A Combinatorial Method

Carbonization at Varying Temperatures of PVA-Derived Nanofibers Fabricated by Electrospinning

Evolution of nanodroplets and fractionated crystallization in thermally annealed electrospun blend fibers of poly(vinylidene fluoride) and polysulfone