Preparation of Crosslinked Polystyrene Nanoparticles/Reduced Graphene Oxide Hybrids Using Electrostatic Self. Assembly and Their Application in Sbr
Yao-ran Chen,Yong Lin,Yi-zhong Chen,Ying Zhang,Lan Liu
DOI: https://doi.org/10.11777/j.issn1000-3304.2016.16116
2016-01-01
Acta Polymerica Sinica
Abstract:Positively charged crosslinked polystyrene (PS) nanoparticles were first synthesized by emulsion polymerization using CTAB as emulsifier, and crosslinked PS nanoparticles/reduced graphene oxide hybrids (PS@ rGO) were fabricated by electrostatic self. assembly, accompanied with in situ reduction. The obtained PS @ rGO hybrids were incorporated into SBR matrix to fabricate SBR/PS@ rGO composites. The structure and morphology of the composites were investigated. The results showed that GO was efficiently reduced by in situ reduction, and the obtained reduced graphene oxide (rGO) exhibited strong pi-pi interactions with PS nanoparticles. PS particles with their size of 60 similar to 70 nm were uniformly adsorbed onto the surface of rGO sheets, which effectively prevented rGO sheets from re. stack and aggregation. Then vulcanization performance tests further indicated that the inclusion of PS@ rGO hybrids not only shortened the curing time (T-c90) by accelerating the vulcanization rate (CRI), but also improved the total crosslinking density of the composites. When 30 phr PS@ rGO were introduced into SBR, the CRI was enhanced by 67. 07%. And as expected, the morphology and performance analysis, and Mooney. Rivlin equation further demonstrated that PS@ rGO hybrids were preferably dispersed in the matrix because of the synergistic effect resulted from PS and rGO, forming a 3D hybrid filler network in the rubber matrix. Also, it was reasonably concluded that the PS served as bridges connecting SBR matrix and rGO, resulting in strong interfacial interactions between PS@ rGO and the rubber matrix. Thus, the improved filler dispersion and enhanced interfacial interactions greatly improved the mechanical performance and abrasion resistance of the SBR composites. For example, SBR/PS @ rGO composites with a lower density exhibited higher mechanical performance and abrasion resistance in comparison with the SiO2 filled composites. These enhanced performances significantly conduce to reducing energy consumption under the dynamic condition, which further makes SBR/PS@ rGO composites very promising in the application of rubber products, such as tire, etc.