Effects of Carbon Black Surface Modification on the Morphology and Properties in Blends with Natural Rubber Studied with High‐Resolution X‐Ray Computed Tomography
Yuting Wang,Wei Jiang,Keran Zhu,Lihui Wu,Liang Chen
DOI: https://doi.org/10.1002/mame.202400019
2024-03-20
Macromolecular Materials and Engineering
Abstract:Compared to normal untreated carbon black filler (figure(b)), the graphitized ones (figure(a)), the aggregate sizes are smaller and more homogeneously dispersing in rubber matrix, but the backbones of filler network are weaker and easily destructing and rearranging during stretching. For oxidized ones (figure(c)), the improvements of surface activities strengthen the filler‐rubber interactions, but decrease resulting in inhomogeneous network structures. To elucidate the specific mechanical impact of carbon black (CB) filler–rubber interactions on reinforcement, CB particles are subjected to graphitization at 1300 °C and oxidation through concentrated nitric acid treatment to modulate their surface activity. Alongside untreated CB particles, the influence of surface activity and the oxygen distribution are investigated to assess their role in shaping CB aggregate structures using X‐ray absorption spectrum (XAS) and X‐ray computed tomography (CT) with spatial resolution of 30 nm. Meanwhile, virgin and modified CBs are blended in natural rubber with varying amounts (10, 30, 50 phr) and the aggregates distributions in rubber are investigated by nano‐CT. Combined with the mechanical properties of rubber composites and parameters of filler networks, the mechanical contributions arising from filler–rubber interactions are quantified. The findings underscore the robust interactions between oxidized CB and rubber matrix, exhibiting a mechanical property enhancement ratio of ≈59.2% at low strains in comparison to normal CB filler. The results indicate the synergies encompass of filler network, rubber chains, and filler–rubber interactions all play important roles for reinforcement, which aligns with the broader understanding of filler–rubber interactions and CB reinforcement mechanisms.
materials science, multidisciplinary,polymer science