Enhancing Devulcanizing Degree and Efficiency of Reclaimed Rubber by Using Alcoholic Amines as the Devulcanizing Agent in Low-Temperature Mechano–Chemical Process
Lei Guo,Lichen Bai,Jinyang Zhao,Kexin Liu,Xingao Jian,Hailin Chai,Fumin Liu,Shouyun Guo,Gongxu Liu,Haichao Liu
DOI: https://doi.org/10.3390/polym16030395
IF: 5
2024-02-01
Polymers
Abstract:Low-temperature mechanical chemical devulcanization is a process that can produce reclaimed rubber with exceptional mechanical properties. However, the inadequacy and low efficiency of the devulcanization have significantly restricted its application. To address the issues, alcoholic amines, including hydroxyethyl ethylenediamine (AEEA), ethanolamine (ETA), and diethanol amine (DEA), are utilized as devulcanizing agents to promote the devulcanization process. Careful characterizations are conducted to reveal the devulcanizing mechanism and to depict the performances of reclaimed rubbers. Results show that the amine groups in the devulcanizing agents can react with sulfur after the crosslink bonds are broken by mechanical shear force, thus blocking the activity of sulfur and introducing hydroxyl groups into the rubber chains. The incorporation of alcoholic amines can enhance the devulcanizing degree and devulcanizing efficiency, reduce the Mooney viscosity, and improve the mechanical and anti-aging performance. When using DEA as the devulcanizing agent, the sol content of reclaimed rubber increases from 13.1% to 22.4%, the devulcanization ratio increases from 82.1% to 89.0%, the Mooney viscosity decreases from 135.5 to 83.6, the tensile strength improves from 14.7 MPa to 16.3 MPa, the retention rate of tensile strength raises from 55.2% to 82.6% after aging for 72 h, while the devulcanization time is shortened from 21 min to 9.5 min, compared with that without using alcoholic amines. Therefore, alcoholic amines exhibit remarkable advantages in the devulcanization of waste rubber, thus indicating a promising direction for the advancement of research in the area of waste rubber reclamation.
polymer science