Enhancing Devulcanizing Degree and Efficiency of Reclaimed Rubber by Using Alcoholic Amines as the Devulcanizing Agent in Low-Temperature Mechano–Chemical Process

Lei Guo,Lichen Bai,Jinyang Zhao,Kexin Liu,Xingao Jian,Hailin Chai,Fumin Liu,Shouyun Guo,Gongxu Liu,Haichao Liu
DOI: https://doi.org/10.3390/polym16030395
IF: 5
2024-02-01
Polymers
Abstract:Low-temperature mechanical chemical devulcanization is a process that can produce reclaimed rubber with exceptional mechanical properties. However, the inadequacy and low efficiency of the devulcanization have significantly restricted its application. To address the issues, alcoholic amines, including hydroxyethyl ethylenediamine (AEEA), ethanolamine (ETA), and diethanol amine (DEA), are utilized as devulcanizing agents to promote the devulcanization process. Careful characterizations are conducted to reveal the devulcanizing mechanism and to depict the performances of reclaimed rubbers. Results show that the amine groups in the devulcanizing agents can react with sulfur after the crosslink bonds are broken by mechanical shear force, thus blocking the activity of sulfur and introducing hydroxyl groups into the rubber chains. The incorporation of alcoholic amines can enhance the devulcanizing degree and devulcanizing efficiency, reduce the Mooney viscosity, and improve the mechanical and anti-aging performance. When using DEA as the devulcanizing agent, the sol content of reclaimed rubber increases from 13.1% to 22.4%, the devulcanization ratio increases from 82.1% to 89.0%, the Mooney viscosity decreases from 135.5 to 83.6, the tensile strength improves from 14.7 MPa to 16.3 MPa, the retention rate of tensile strength raises from 55.2% to 82.6% after aging for 72 h, while the devulcanization time is shortened from 21 min to 9.5 min, compared with that without using alcoholic amines. Therefore, alcoholic amines exhibit remarkable advantages in the devulcanization of waste rubber, thus indicating a promising direction for the advancement of research in the area of waste rubber reclamation.
polymer science
What problem does this paper attempt to address?
### Problems the paper attempts to solve This paper aims to solve the problems of insufficient desulfurization degree and low efficiency in the low - temperature mechanochemical desulfurization process of recycled rubber. Specifically: 1. **Insufficient desulfurization degree**: Although the traditional low - temperature mechanochemical desulfurization method can produce recycled rubber with excellent mechanical properties, its desulfurization degree is relatively low, which limits its wide use in practical applications. 2. **Low desulfurization efficiency**: The desulfurization process under low - temperature conditions has low efficiency, resulting in a long production time and affecting production efficiency and economy. To overcome these problems, the author proposes a new method, that is, using alkanolamine compounds (including hydroxyethylethylenediamine (AEEA), ethanolamine (ETA) and diethanolamine (DEA)) as desulfurizing agents to promote the low - temperature mechanochemical desulfurization process. Through the introduction of these compounds, the author hopes to increase the desulfurization degree and desulfurization efficiency, while reducing the Mooney viscosity of rubber and improving its mechanical properties and anti - aging properties. ### Main research contents 1. **Analysis of desulfurization mechanism**: - The amino group in alkanolamine compounds can react with the cross - linking bonds after fracture, preventing the activity of sulfur, thereby preventing re - cross - linking. - The introduction of hydroxyl groups can reduce the Mooney viscosity of rubber, improve plasticity and desulfurization efficiency. 2. **Experimental methods**: - Use different alkanolamine compounds to conduct desulfurization experiments and compare their effects on the desulfurization degree and efficiency. - Characterize the structure and properties of desulfurized rubber by means of X - ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), etc. 3. **Experimental results**: - When DEA is used as a desulfurizing agent, the sol content of recycled rubber increases from 13.1% to 22.4%, the desulfurization ratio increases from 82.1% to 89.0%, the Mooney viscosity decreases from 135.5 to 83.6, the tensile strength increases from 14.7 MPa to 16.3 MPa, the tensile strength retention rate after aging for 72 hours increases from 55.2% to 82.6%, and the desulfurization time is shortened from 21 minutes to 9.5 minutes. ### Conclusion By using alkanolamine compounds as desulfurizing agents, the desulfurization degree and efficiency of recycled rubber in the low - temperature mechanochemical desulfurization process can be significantly improved, while its mechanical properties and anti - aging properties are also improved. This method provides a new direction for waste rubber recycling and has important research and application values.