Abstract:High strength and ductile nickel aluminum bronze (NAB) alloys were produced by heavy warm rolling (HWR) and subsequent annealing at various temperatures. The effect of annealing temperatures ranging from 473 K to 1173 K (200 °C to 900 °C) on the microstructure, mechanical, and electrochemical properties of these HWRed NAB alloys was studied. The results show that the evolution of microstructure and mechanical behavior can be divided into three distinct stages with the increasing annealing temperature. When annealed below 500 °C (Stage A), the HWRed samples exhibit ultrahigh strength and good ductility. Such remarkable tensile properties are mainly attributed to the ultrafine α grains and nano k precipitates. Part of the α phase recrystallized, contributing to a further decrease in the average grain size. An ultrahigh ultimate strength of 1363 MPa and uniform elongation of 6.0 pct can be obtained when the alloy is annealed at 400 °C for 1 hour. When annealed at 600 °C and 700 °C (Stage B), a prominent strength–ductility combination with a yield strength of about 1000 MPa and an elongation of about 15 pct can be achieved, mainly due to the uniform ultrafine microstructures and the high-density annealing twins. Some nano k phases with grain size less than 20 nm precipitate dispersedly in α grains, which may also be a significant strengthening factor. When the temperature reaches above 800 °C (Stage C), the yield strength reduces dramatically, while the elongation and ultimate strength further increase. At this stage, the matrix transforms from single ultrafine α grains into a fine-grained ( α + β ′) duplex structure with high-density ultrafine annealing twins inside α grains. It is found that the mechanical properties of the HWRed and annealed alloys are greatly enhanced, while the electrochemical stability almost shows no deterioration compared with the undeformed coarse-grained alloys. This indicates that HWR and subsequent annealing is an effective strategy for preparing bulk NAB alloys with high performance.

Enhancing Mechanical Properties and Corrosion Resistance of Nickel-Aluminum Bronze Via Hot Rolling Process

Ultra-strong Nickel Aluminum Bronze Alloys with Ultrafine Microstructures by Continuous Heavy Hot Rolling

The Role of Nickel in Mechanical Performance and Corrosion Behaviour of Nickel-Aluminium Bronze in 3.5 Wt.% NaCl Solution

Tailoring microstructure of a nickel aluminium bronze by hot extrusion and its impact on mechanical and corrosion behaviour

Effect of Microstructure on the Mechanical and Corrosion Behaviors of a Hot-Extruded Nickel Aluminum Bronze

Effect of Annealing Temperature on Microstructure and Properties of a Heavy Warm Rolled Nickel Aluminum Bronze Alloy

Effect of Heat Treatment on Microstructure Evolution and Erosion–corrosion Behavior of a Nickel–aluminum Bronze Alloy in Chloride Solution

Experimental investigation on wear resistance and corrosion behavior of nickel-aluminum bronze alloy fabricated by wire-arc additive manufacturing

Correlation between microstructure and corrosion and cavitation erosion behaviors of nickel aluminum bronze

Microstructure evolution during the heavy warm rolling of a nickel aluminum bronze

Effect of Heat Treatment on Microstructure and Properties of Hot-Extruded Nickel-Aluminum Bronze

Effect of Al/Ni Ratio on the Microstructure and Properties of Nickel-Aluminum Bronze Alloys

Investigation of Microstructure and Mechanical Properties of Hot Worked Nial Bronze Alloy with Different Deformation Degree

Improving mechanical anisotropy and corrosion resistance of extruded AA7075 alloy by warm cross rolling and annealing

Modification of Cold-Sprayed Aluminum Coating on Nickel-Aluminum Bronze by Micro-Arc Oxidation

Microstructure, Mechanical and Tribological Properties of Nickel-Aluminium Bronze Alloys Developed Via Gas-Atomization and Spark Plasma Sintering

Multiple cycles of combined cold rolling and short-time annealing on the microstructure and properties evolution of NiAl bronze

Recent Advances Of Nickel-Aluminum Bronze (Nab)

Erosion-corrosion behavior of Ni-Al-Cu coating on nickel-aluminium bronze alloy in 3.5 wt.% NaCl solution

Electrochemical Corrosion Mechanisms of Nickel-Aluminium Bronze with Different Nickel Contents Using the Rotating Disc Electrode

Additive Manufacturing Nickel-Aluminum Bronze Alloy Via Wire-Fed Electron Beam Directed Energy Deposition: Enhanced Mechanical Properties and Corrosion Resistance Compared to As-Cast Counterpart