Abstract:As-sintered multi-main-phase Nd-Ce-Fe-B permanent magnets typically exhibit a higher coercivity than as-sintered single-main-phase Nd-Ce-Fe-B magnets with identical content of Ce. To clarify the microstructural features that are relevant to the coercivity, as-sintered multi-main-phase Nd-Ce-Fe-B permanent magnets are characterised by high-resolution magnetic force microscopy and atom probe tomography down to the atomic scale. Though inhomogeneous distribution of rare earth elements (Nd, Pr, and Ce) is observed inside 2:14:1 matrix grains, Ce atoms unexpectedly show similar partitioning behaviour (∼14–27% of rare earth element) at the edge of these grains in the vicinity of rare earth-rich grain boundary compared with as-sintered single-main-phase Nd-Ce-Fe-B magnets with a 20% Ce substitute of Nd and Pr. By contrast, the observation of stripe-liked magnetic domains pinned at the grain boundaries and a thin (Nd,Pr,Ce)-rich grain boundary with a composition of Nd9.9Pr2.6Ce19.0Fe65.3Co1.9Balance1.3 (at.%) jointly indicates the enrichment of Ce in grain boundaries benefit to the magnetic isolation of neighbouring matrix grains in the as-sintered state. Unusual Ce-rich clustering regions are also observed in the grain boundary, which also contribute to the coercivity enhancement. The segregation of Ce, Co, and Cu and rare-earth-Cu clusters are only observed at the interface between rare earth-Cu rich phase and matrix phase while no obvious elemental segregation and clusters are observed at the interface between the rare earth-Ga rich phase and matrix phase, suggesting the occurrence of rare earth-Cu rich phase may be one of the reasons for achieving high coercivity. These findings offer fresh insights into the as-sintered multi-main-phase Nd-Ce-Fe-B permanent magnets.

Evolution of REFe2 (RE = Rare Earth) Phase in Nd-Ce-Fe-B Magnets and Resultant Ce Segregation

Exploring the distinctive role of REFe 2 (RE=rare earth) phase in sintered and hot-deformed Ce-containing Nd-Fe-B magnets

Research on the La/Ce-rich multi-main-phase RE-Fe-B permanent magnetic materials

Effects of Refe2 on Microstructure and Magnetic Properties of Nd-Ce-Fe-B Sintered Magnets

Study on Ce2Fe14B-based sintered magnets with Ce/RE> 80

Promoting the La Solution in 2:14:1-Type Compound: Resultant Chemical Deviation and Microstructural Nanoheterogeneity

Concurrent Improvements of Corrosion Resistance and Coercivity in Nd-Ce-Fe-B Sintered Magnets Through Engineering the Intergranular Phase

Comparison of (pr, Nd)H Grain Boundary Restructuring and Diffusion on the Magnetic Properties of Nd–La–Ce–Fe–B Sintered Magnet

Magnetic performance change of multi-main-phase Nd–Ce–Fe–B magnets by diffusing (Nd, Pr)H x

Crucial Role of the REFe2 Intergranular Phase on Corrosion Resistance of Nd-La-Ce-Fe-B Sintered Magnets

A Reliable Route for Relieving the Constraints of Multi-Main-phase Nd–La–Ce–Fe–B Sintered Magnets at High La–Ce Substitution: (pr, Nd)H Grain Boundary Diffusion

Grain boundary restructuring of multi-main-phase Nd-Ce-Fe-B sintered magnets with Nd hydrides

Enhanced Coercivity of Nd-Ce-Fe-B Sintered Magnets by Adding (nd, Pr)-H Powders

Influence of Ce Content on the Rectangularity of Demagnetization Curves and Magnetic Properties of Re-Fe-B Magnets Sintered by Double Main Phase Alloy Method

Cu-mediated Grain Boundary Engineering in Nd–Ce–Fe–B Nanostructured Permanent Magnets

Unusual surface microstructural evolution of Nd–Ce–Fe–B sintered magnets by (Nd, Pr)Hx grain boundary diffusion

The Effects of Forming CeFe2 on Phase Structure and Magnetic Properties in Ce-Rich Nd-Ce-Fe-B Permanent Magnetic Materials

Atomic scale insights into the segregation/partitioning behaviour in as-sintered multi-main-phase Nd-Ce-Fe-B permanent magnets

Microstructure and magnetic performance of Nd–Y–Ce–Fe–B sintered magnets after annealing

Strategy to improve magnetic property of sintered (Nd, Ce)–Fe–B magnets: Moderate replacement of cerium with lanthanum

Strategy for Co‐Enhancement of Remanence–Coercivity of RE‐Fe‐B Sintered Magnets with High Ce‐Content: Appropriate La Substitution