Abstract:Polymer-clay nanocomposite gels (NC gels) consisting of poly(N-isopropylacrylamide) (PNIPA) and inorganic clay (hectorite) were investigated in terms of their optical and swelling/deswelling properties. Depending on the clay concentration (C-clay), NC gels exhibit unique changes in optical transmittance, optical anisotropy, and swelling/deswelling behaviors, all of which were distinct from those of chemically cross-linked hydrogels (OR gels). The optical transparency and its temperature-induced change differed greatly between NC and OR gels. The decrease in transmittance associated with the coil-to-globule transition of PNIPA occurred at higher temperatures than the normal transition temperature in NC gels as the clay concentration increased. On the assumption of the uniform and random dispersion of exfoliated clay platelets, the critical C-clay (C*(clay)) for spontaneous clay aggregation (layer stacking) in NC gels was calculated to be 10 x 10(-2) mol/L H2O. C*(clay) was consistent with the experimental results, including the mechanical properties of strength and modulus, the transparency changes induced by temperature, and the appearance of optical anisotropy. Optical anisotropy was observed in NC gels with clay concentrations above C*(clay), and by increasing the water content, it could be reversibly changed to isotropy when C-clay was close to C*(clay). The swelling of NC gels at 20 degrees C and their deswelling at 50 degrees C were both depressed greatly with increasing C-clay. Furthermore, NC gels with C-clay higher than that of NC 12 gel exhibited swelling even at 50 degrees C, and it is expected that NC gels whose volume remains unchanged regardless of temperature can be produced by further increasing C-clay. All of these unique changes in the properties of NC gels can be explained by the partial phase separation due to the coil-to-globule transition of PNIPA and the dispersion morphology of clay platelets.

Synthesis and Characterization of Temperature and Light Double Responsive Organic/Inorganic Nanocomposite Hydrogels Crosslinked by Clay

Synthesis and Characterization of Ph and Temperature Double-Sensitive Nanocomposite Hydrogels Consisting of Poly(Dimethylaminoethyl Methacrylate) and Clay

The Unique Optical and Physical Properties of Soft, Transparent, Stimulus-Sensitive Nanocomposite Gels

Swelling, Elasticity, and Spatial Inhomogeneity of Poly(N-isopropylacrylamide)/Clay Nanocomposite Hydrogels

Thermosensitive Poly(N-isopropylacrylamide-co-acrylonitrile) Hydrogels with Rapid Response

A Novel Fast Responsive Thermo-Sensitive Poly(n-Isopropylacrylamide)-clay Nanocomposites Hydrogels Modified by Nanosized Octavinyl Polyhedral Oligomeric Silsesquioxane.

Preparation and Characterization of Dual-Sensitive Double Network Hydrogels with Clay As a Physical Crosslinker

Responsiveness and Release Characteristic of Semi-IPN Hydrogels Consisting of Nano-Sized Clay Crosslinked Poly(Dimethylaminoethyl Methacrylate) and Linear Carboxymethyl Chitosan

pH/temperature double responsive behaviors and mechanical strength of laponite‐crosslinked poly(DEA‐co‐DMAEMA) nanocomposite hydrogels

Tunable Optical and Swelling/Deswelling Properties Associated with Control of the Coil-to-Globule Transition of Poly(N-isopropylacrylamide) in Polymer−Clay Nanocomposite Gels

Temperature/pH Dual-Responsive Poly (N-Isopropylacrylamide)/chitosancoated Luminescent Composite Nanospheres: Fabrication and Controllable Luminescence

A novel nanocomposite hydrogel with precisely tunable UCST and LCST.

Responsiveness, Swelling, and Mechanical Properties of PNIPA Nanocomposite Hydrogels Reinforced by Nanocellulose

Triply-responsive (thermo/light/pH) copolymeric hydrogel of N-isopropylacrylamide with an azobenzene-containing monomer

Copolymer Nanocomposite Hydrogels: Unique Tensile Mechanical Properties and Network Structures

Synthesis and Characterization of Water-Soluble POSS Hybrid Inorganic/Organic PDMAEMA Nanocomposite Hydrogels

SYNTHESIS AND PROPERTIES OF POLY (N-ISOPROPYLACRYLAMIDE)-CLAY NANO-HYDROGEL

The preparation and characteristic of robust inorganic/organic IPN nanocomposite hydrogels with fast response rate

Synthesis and Characterization of Poly(n-Tert-butylacrylamide-co-acrylamide) Hydrogel with Enhanced Responsive Properties

Mechanical Behavior of a Terpolymer-Based Ph- and Temperature-Responsive Hydrogel

Radiation synthesis of polymer/clay nanocomposite hydrogels with high mechanical strength