Abstract:The ground state of Ce~(3+) is 4f~15d~0,which have only one 4f electron on the configuration.For this reason,the excitation spectrum of Ce~(3+) ion directly shows the energy state of 5d level.Ce~(3+) ion can be used as a probe to investigate the f-d transitions of other rare-earth ions in same host lattice sites,since the simila-(rity) of the crystal-field effect on the 5d states of different rare earth ions in the sites.The phosphor,Ce~(3+) ion activated tetra-borate SrB_4O_7,was prepared by high temperature solidstate reaction technique in present paper.Na~+ ion was added to balance the electronic charge due to the different electronic charge value between Ce~(3+) and Sr~(2+) ions.The XRD patterns of the sample Sr_(0.96)Ce_(0.02)Na_(0.02)B_4O_7 are in good line with the JCPDS standard card 15-801(SrB_4O_7).The VUV(vacuum ultraviolet) excitation and emission spectra were measured at the VUV spectroscopy experimental station on beam line 3B1B,Beijing Synchrotron Radiation Facilities(BSRF),under normal operating conditions(2.2 GeV,100 mA) at 293 K.The spectroscopic properties of this phosphor are investigated in the wavelength region 130~400 nm.The host-related Absorption is found to be about 155 nm.The five bands corresponding to the 4f~1→4f~05d~1 transitions of Ce~(3+) ions are identified as 277,242,228,217 and 202 nm in the host lattices.Therefore,the 5d crystal field splitting and the bary-(center) of Ce~(3+) in the host lattice are calculated to be 13.4×10~3 and 43.4×10~3 cm~(-1),respectively.The doublet emission bands of Ce~(3+) in the host lattice are observed at 293 and 313 nm.Hence,the Stokes shift is(1 971) cm~(-1).Because SrB_4O_7 and SrBPO_5 share iso-structural characteristics: the cations are same,and all of anions are tetrahedral AO_4(A = B,P).The spectroscopic properties of Ce~(3+) in these host lattices are compared and discussed qualitatively.

VUV–UV Photoluminescence Spectra of Strontium Orthophosphate Doped with Rare Earth Ions

Vuv-Uv Excited Luminescent Properties of Calcium Borophosphate Doped with Rare Earth Ions

The Optical Spectroscopic Properties of Rare Earth-Activated Barium Orthophosphate in VUV-Vis Range

VUV–UV Spectroscopic Properties of RE (RE3+ = Ce, Eu and Tb)-doped KMLn(PO4)2 (M2+ = Ca, Sr; Ln3+ = Y, La, Lu)

Vuv And Eu-L-3 Edge Xanes Spectra Of Europium-Doped Strontium Tetraborate Prepared In Air

Photoluminescence of Ce3+, Pr3+ and Tb3+ activated Sr3Ln(PO4)3 under VUV-UV excitation

XAFS at Eu–L3 edge and UV–VUV excited luminescence of europium doped strontium borophosphate prepared in air

VUV Spectrum of Ce~(3+) Activated SrB_4O_7

Photoluminescence of Srgdga3o7 : Re (re = Ce3+, Pr3+, Tb3+) under Vuv-Uv Excitation

VUV Spectroscopic Properties of Ce3+ and Pr3+-doped AREP2O7-type Alkali Rare Earth Diphosphates (a=na, K, Rb, Cs; RE=Y, Lu)

UV–VUV excited luminescence of SrBPO5:Sm phosphor prepared in air

VUV-UV-vis Photoluminescence, X-ray Radioluminescence and Energy Transfer Dynamics of Ce3+ and Eu2+ in Sr2MgSi2O7.

Comparative investigations of the crystal structure and photoluminescence property of eulytite-type Ba3Eu(PO4)3 and Sr3Eu(PO4)3.

Photoluminescence of Ce3+, Tb3+, Sm3+ or Gd3+ Activated Ba3BP3O12 under the VUV and UV Excitation

Spectroscopic properties of Ce3+ doped MBPO5 (M = Ca, Sr, Ba) under VUV excitation

VUV–UV Excited Luminescent Properties of LnCa4O(BO3)3:RE3+ (ln=y, La, Gd; Re=Eu, Tb, Dy, Ce)

On the Energy Dependence of the PL of RE Ions in LuBO3:RE (RE = Ce, Eu, Gd, or Tb)

Luminescence of Ce3+ and Pr3+ Doped Sr2Mg(BO3)2 under VUV–UV and X-ray Excitation

VUV Excited Luminescence of Europium Activated Calcium Borophosphate Prepared in Air

The VUV–vis Spectroscopic Properties of Phosphors Ca3Gd2(1−x)Ln2x(BO3)4 (ln3+=ce, Sm, Eu, Tb)

The VUV-vis luminescent properties of Ln3+ (Ln = Ce, Pr, Tb) in Sr0.96Na0.02Ln0.02B4O7