Abstract:Abstract Based on a continuous-domain model, capable of accessing the spatiotemporal scales relevant to fuzz formation on the surface of plasma-facing component (PFC) tungsten, we report self-consistent simulation results that elucidate the effects of elastic softening and helium (He) accumulation kinetics on the surface morphological response of PFC tungsten. The model accounts for the softening of the elastic moduli in the near-surface region of PFC tungsten, including both thermal softening at high temperature and softening due to He accumulation upon He implantation. The dependence of the elastic moduli on the He content follows an exponential scaling relation predicted by molecular-dynamics simulations, while the He content in the near-surface region of PFC tungsten evolves according to a first-order saturation kinetics, consistent with experimental and simulation results reported in the literature. We establish that this elastic softening accelerates both nanotendril growth on the PFC surface and the onset of fuzz formation. We also explore the role of the rate of He accumulation to a saturation level in the near-surface region of irradiated tungsten in the onset of fuzz formation. For PFC tungsten surfaces such as W(110) where, under typical irradiation conditions, the characteristic time scale for stress-driven surface diffusion is comparable to the characteristic time scale for He accumulation, we find that accelerating the rate of He accumulation accelerates the growth rate of nanotendrils emanating from the surface. Additionally, we present a systematic parametric study of the PFC surface morphological response to explore its dependence on the He accumulation kinetics that is controlled by the irradiation conditions for low-energy implantation. Finally, we introduce an incubation time for nanotendril growth on the PFC surface, a concept equivalent to that of incubation fluence discussed in the literature, to predict and explain the minimum exposure time required to observe fuzz formation on PFC tungsten surfaces.

Effect of intermittent He/D ion irradiations on W nano-fuzz growth over W targets

Initial growth of tungsten fuzz induced by bubble-driven surface stress layer under helium irradiation

Nanostructured fuzz growth on tungsten under low-energy and high-flux He irradiation

The effect of Ar+ impurity on W nano-fuzz growth over polycrystalline W targets

He nanobubble driven W surface growth during low-energy He ion irradiations

The effect of W fuzz growth on D retention in polycrystalline W

He-ion induced surface morphology change and nanofuzz growth on hot tungsten surfaces

The rapid growth of He nanobubbles in vicinity of the axis of W nanofibers under fusion-relevant He ion irradiations

Tensile stress-driven cracking of W fuzz over W crystal under fusion-relevant He ion irradiations

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Tungsten fuzz: Deposition effects and influence to fusion devices

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Effects of elastic softening and helium accumulation kinetics on surface morphological evolution of plasma-facing tungsten

Effect of Surface Quality on Hydrogen/helium Irradiation Behavior in Tungsten

Modelling of physical sputtering properties during tungsten fuzz growth under various impact energies on NAGDIS-II

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

The fracture and merging of W nanofibers under low-energy He ion irradiations at an elevated temperature

Effects of Low Energy and High Flux Helium/Hydrogen Plasma Irradiation on Tungsten As Plasma Facing Material

An improved model for the prediction of He bubbles driven W fuzz growth at different temperatures

The Influence of Coherent Oxide Interfaces on the Behaviors of Helium (He) Ion Irradiated ODS W

Erosion dynamics of tungsten fuzz during ELM-like heat loading