Abstract:Undercooling experiments were performed with Co-10%Sb and Co-60.5%Sb alloys in order to investigate the dendrite growth kinetics within the solutal and thermal diffusion-controlled growth regimes. These alloy compositions correspond to the two extremes of eutectic horizontal line and hence have the broadest equilibrium freezing temperature ranges. The maximum undercoolings obtained for these alloys are 274 K (0.16 T-L) and 168 K (0.11 T-L), which have either approached or exceeded their equilibrium freezing temperature ranges. The dendrite growth velocities were measured as a function of undercooling. The experimental results were analyzed within the current theories of dendritic growth. The results indicate that alpha-Co solid solution phase attains a growth velocity of 60 m s(-1) at 274 K undercooling, whereas beta-CoSb intermetallic compound grows more slowly with a maximum velocity of 12 m s(-1). The investigations reveal a transition from solute diffusion-controlled growth to thermal diffusion-controlled growth by the onset of solute trapping at a critical undercooling. It is approximately 150 K in the case of Co-10%Sb alloy and 130 K for Co-60.5%Sb alloy. A 'dendrite-equiaxed' morphological transition is initiated once these alloys are undercooled by more than 100 K. This is interpreted within a recently developed model of dendrite fragmentation as a Rayleigh-like instability of rapidly growing dendrites. (C) 1997 Elsevier Science S.A.

Rapid Growth of Primary Dendrite in Highly Undercooled Copper-Antimany Alloy

High Undercooling and Rapid Dendritic Growth of Cu-Sb Al-Loy in Drop Tube

Solute Diffusion Controlled Dendritic Growth under High Undercooling Conditions

Rapid Solidification Mecha-Nism of Ag_(60)Sb_(34)Cu_(6) Ternaryalloy in Drop Tube

Rapid Solidification Mechanism of Ag60Sb34Cu6 Ternary Alloy in Drop Tube

Dendritic Growth Characteristics of Cu-Rich Zone Within Phase Separated Fe<sub>50</sub>Cu<sub>50</sub> Alloy

Rapid Eutectic Growth During Free Fall

Rapid Crystal Growth in Undercooled Hypoeutectic Cu-Sb Alloys

Dendrite growth during rapid solidification of Co-Sb alloys

Nucleation and growth of βCu3Sb intermetallic compound in undercooled Cu–31% Sb eutectic alloy

Rapid Dendritic Growth Within an Undercooled Ni–Cu–Fe–Sn–Ge Quinary Alloy

RAPID SOLIDIFICATION OF UNDERCOOLED Co_(85)Cu_(15) HYPOPERITECTIC ALLOY

A Comparative Study of Dendritic Growth Within Undercooled Liquid Pure Fe and Fe50Cu50 Alloy

Dendritic and Eutectic Growth in Sb60Ag20Cu20 Ternary Alloy

Liquid Phase Separation and Rapid Dendritic Growth of Undercooled Ternary Fe60Co20Cu20 Alloy

Primary Dendrite Growth of Co3Sn2 Intermetallic Compound in Rapidly Solidified Ternary Co35Cu35Sn30 Alloy

Liquid Phase Separation and Rapid Dendritic Growth of Highly Undercooled Ternary Fe62.5cu27.5sn10 Alloy

Rapid Dendritic Growth of Al-Ge Hypoeutectic Alloy in a Drop Tube

Dendritic Growth and Solute Trapping in Rapidly Solidified Cu-based Alloys

Microstructural characterization of cobalt–antimony eutectic alloy droplets solidified in drop tube

Rapid Dendritic Growth in Highly Undercooled Ternary Ni-Cu-Co Alloy