Abstract:Randomness in the void distribution within a ductile metal complicates quantitative modeling of damage following the void growth to coalescence failure process. Though the sequence of micro-mechanisms leading to ductile failure is known from unit cell models, often based on assumptions of a regular distribution of voids, the effect of randomness remains a challenge. In the present work, mesoscale unit cell models, each containing an ensemble of four voids of equal size that are randomly distributed, are used to find statistical effects on the yield surface of the homogenized material. A yield locus is found based on a mean yield surface and a standard deviation of yield points obtained from 15 realizations of the four-void unit cells. It is found that the classical GTN model very closely agrees with the mean of the yield points extracted from the unit cell calculations with random void distributions, while the standard deviation $\textbf{S}$ varies with the imposed stress state. It is shown that the standard deviation is nearly zero for stress triaxialities $T\leq1/3$, while it rapidly increases for triaxialities above $T\approx 1$, reaching maximum values of about $\textbf{S}/\sigma_0\approx0.1$ at $T \approx 4$. At even higher triaxialities it decreases slightly. The results indicate that the dependence of the standard deviation on the stress state follows from variations in the deformation mechanism since a well-correlated variation is found for the volume fraction of the unit cell that deforms plastically at yield. Thus, the random void distribution activates different complex localization mechanisms at high stress triaxialities that differ from the ligament thinning mechanism forming the basis for the classical GTN model. A method for introducing the effect of randomness into the GTN continuum model is presented, and an excellent comparison to the unit cell yield locus is achieved.

An Independent Derivation and Verification of the Voids Nucleation Failure Mechanism: Significance for Materials Failure

An Evaluation of the Failure Modes Transition and the Christensen Ductile/brittle Failure Theory Using Molecular Dynamics

Instability Analysis and Rate-Dependent Failure Criteria for Adiabatic Shear Band Propagation of Ti-6al-4v

Tensile Failure Modes in Nanograined Metals with Nanotwinned Regions

A unified strength criterion for two-dimensional materials via bond failure analysis

Failure of Griffith Theory on Prediction of Theoretical Strength of Ideal Materials

The mechanistic origins of heterogeneous void growth during ductile failure

Cylindrical Void in a Rigid-Ideally Plastic Single Crystal. Part I: Anisotropic Slip Line Theory Solution for Face-Centered Cubic Crystals

Model of Void Nucleation on Grain Boundaries in Dynamic Failure of Ductile Metals Incorporating Interface Incompatibility

Derivation of effective theories for thin 3D nonlinearly elastic rods with voids

A micro-mechanics based extension of the GTN continuum model accounting for random void distributions

Ductile failure modeling

A self-consistent void-based rationale for hydrogen embrittlement

Theoretical Models of Void Nucleation and Growth for Ductile Metals under Dynamic Loading: A Review

Analysis of Metallic Ductile Fracture by extended Gurson models

A unified model for yield strength and plastic behavior of nanovoid evolution in tungsten based on molecular dynamics simulations

Sensitivity of void mediated failure to geometric design features of porous metals

A Mechanism of Failure in Shear Bands

An Exploration Toward A Unified Failure Criterion

Continuum damage mechanics modelling incorporating stress triaxiality effect on ductile damage initiation