Temperature-Dependent Transformation from Whisker- to Nanoparticle-Strengthened Composite Interface in the Al2o3/Ag-Based Alloy System and Mechanical Properties of the Joints
Yifeng Wang,Jian Cao,Zhijie Wang,Zhe Chen,Xiaoguo Song,Jicai Feng
DOI: https://doi.org/10.1016/j.matchar.2015.09.015
IF: 4.537
2015-01-01
Materials Characterization
Abstract:Al4B2O9-whisker-coated Al2O3 ceramics were bonded by AgCu–4.5wt.%Ti alloy in vacuum. The microstructure of the whisker-coated Al2O3 joints was investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. A continuous (Cu,Al)3Ti3O layer formed against the alloy at lower bonding temperatures, and a complex transition zone bordering the whiskers was observed, which consisted of Ag nanoparticles, titanium oxides, TiB2, (Cu,Al)3Ti3O nanoparticles and possible Ag3Al. As the bonding temperature increased, the Al2O3/AgCuTi interface was found to transform from whisker- to nanoparticle-strengthened composite region. Bend test results revealed that both the whiskers grown on Al2O3 and the dispersive nanoscale products in the alloy played positive roles in improving the joint properties. The maximum bend strength of the whisker-coated Al2O3 joints was 313MPa at the bonding temperature of 820°C.