Abstract:Poly(lactide-co-glycolide) (PLGA) copolymers are the most prevalent materials for tissue engineering applications. To mimic the real microenvironment of extracellular matrix (ECM) for cell growth, nanofibrous PLGA scaffolds are preferred. PLGA5050 (in which the molar ratio of lactidyl to glycolidyl units is 50:50), which is an utterly amorphous polymer, was first reported to be made into nanofibrous networks (fiber diameter around 500nm) using phase separation from PLGA5050/THF solutions in this study. The concentration of polymeric solution had significant effects on fiber diameter and unit length. Nonsolvent (e.g. H2O) was unnecessary to form the PLGA5050 gel, which was critical to nanofibrosis, as if the environmental temperature for gelation occurrence was low enough (−70°C). The physical crosslinks to stabilize the PLGA5050/THF gel were believed to be GA segments along the backbone owing to their inferior solubility in THF. The addition of H2O would cause adverse effects of liquid–liquid phase separation and nanofibrosis failure owing to the hydrophilicity of glycolidyl units. Associating with the phase separation method, particle-leaching technique was applied to fabricate three-dimensional scaffolds with macroporous and nanofibrous structures. To ensure the occurrence of nanofibrosis on macropore walls, the temperature of salt particles should be best lowed to −70°C beforehand. Accordingly, scaffolds prepared under varied parameters exhibited different nanofiber and pore morphologies, which affected the pore size, porosity, specific surface area, water contact angle and protein adsorption ability etc. The preliminary cell (MC3T3-E1) culture confirmed the cell ingrowth into the macroporous and nanofibrous PLGA5050 scaffolds in comparison with the solely nanofibrous matrixes. This kind of bi-scaled three dimensional matrixes can be superior candidate scaffolds for tissue engineering applications.

Fabrication of TiO2 Nanotubes/PLGA Composite Scaffolds Materials

Nanocomposites of poly(l-lactide) and surface-grafted TiO2 nanoparticles: Synthesis and characterization

Poly(lactide-co-glycolide)/titania Composite Microsphere-Sintered Scaffolds for Bone Tissue Engineering Applications.

Porous Poly(L-Lactic Acid) Scaffold Reinforced by Titanium Dioxide Nanoparticles

Preparation and characterization of nano-TiO2/polylactide composites

Preparation, characterization, and properties of TiO<sub>2</sub>/PLA nanocomposites by in situ polymerization

Fabrication and Characterization of Polylactic Acid Electrospun Scaffolds Modified with Multi-Walled Carbon Nanotubes and Hydroxyapatite Nanoparticles

Fabrication Of Bioactive Scaffold Of Poly(Epsilon-Caprolactone) And Nanofiber Wollastonite Composite

Wettability, Topography and Chemistry of Composite PLGA/CaP/Ti Scaffolds for Targeted Drug Delivery

Surface Modification Of Halloysite Nanotubes With L-Lactic Acid: An Effective Route To High-Performance Poly(L-Lactide) Composites

Preparation and characterization of PLGA/TiO2 nano drug delibery carriers

Carbon nanotubes perpendicularly grown on graphene oxide nanosheets derived from metal-organic frameworks: Synergistic reinforcement of poly(L-lactic acid) scaffold

Synergistic fabrication of micro-nano bioactive ceramic-optimized polymer scaffolds for bone tissue engineering by in situ hydrothermal deposition and selective laser sintering

Macroporous and nanofibrous poly(lactide-co-glycolide)(50/50) scaffolds via phase separation combined with particle-leaching

Fabrication of Nanostructured PLGA Scaffolds Using Anodic Aluminum Oxide Templates

Porogen-induced Surface Modification of Nano-Fibrous Poly(l-Lactic Acid) Scaffolds for Tissue Engineering

Surface Engineering of Nano-fibrous Biodegradable Poly(L-lactic acid) Scaffolds for Tissue Engineering

Incorporation of Tripolyphosphate Nanoparticles into Fibrous Poly(Lactide-Co-Glycolide) Scaffolds for Tissue Engineering

Electrospun biodegradable scaffolds based on poly (ε-caprolactone)/gelatin containing titanium dioxide for bone tissue engineering application; in vitro study

Novel TiO2 nanotubes films with silk fibroin substrate

Nano-TiO2 Modified Wheat Straw/Polylactic Acid Composites Based on Synergistic Effect Between Interfacial Bridging and Heterogeneous Nucleation