Effect of Process Parameters on Mechanical Properties of Ti/Zn/Al Joint Welded by Friction Stir Welding

Zhang Xin,Chen Yuhua,Wang Shanlin

2017-01-01

Rare Metal Materials and Engineering

Abstract:2A14 aluminium alloy of 3 mm in thickness and TC4 titanium alloy were welded by friction stir welding (FSW) with a 0.05 mm Zn ribbon as the intermediate layer. The effects of process parameters on macro-morphology, microstructure and mechanical properties of the joints were studied. The results indicate that the well-formed joints can be fabricated by friction stir welding with the parameters of welding velocity 75 mm/min, rotation speed 375 similar to 950 r/min and offset 2.5 mm between the center of pin and interface of the two plates. The surface roughness decreases and then increases with the rotation speed increasing, while the tensile strength of the joints decreases gradually. However, as the welding velocity increases from 60 min/min to 95 mm/min, the fins of the weld become less gradually. When the welding velocity, rotation speed and offset are 75 mm/min, 375 r/min and 2.5 mm, respectively, the maximum tensile strength is up to 237.3 MPa, nearly 56.7% of that of the aluminum alloy.