Influence of Solution Treatment on the Microstructure and Mechanical Property of Ti60 Alloy

Wenzhong Luo,Feng Sun,Xiaohua Zhao,Xiaoyuan Zhang,Jinwen Lei

2017-01-01

Rare Metal Materials and Engineering

Abstract:Both of the α'and α+α'martensite microstructures of Ti60 alloy as high temperature titanium alloy used up to 600 ℃ were obtained by solution treatments at different temperatures.The morphologies of the two microstructures were compared as well as the tensile properties at room temperature,300 ℃ and 600 ℃.The results indicate that all the β phase transforms to α'phase during quenching,and only about 10％ primary α phase retains in the α+α'microstructure.The little decrease of strength and great increase of ductility can be attributed to the partial solution of primary α phase.The size of dimple observed on the fracture of specimens with α+α'microstructure at room temperature is larger than that with α'microstructure.Because the retained primary α phase dedicates to the refinement ofβ grains,leading to the disturbance of expansion of cracks by increasing the length of grain boundaries.The influence of the primary α phase on the tensile properties decreases with the increasing of the tensile temperature.