Influence of the Substitution Ce for La on Structural and Electrochemical Characteristics of La0.75-xCexMg0.25Ni3Co0.5 (x=0, 0.05, 0.1, 0.15, 0.2 At. %) Hydrogen Storage Alloys
Wei Lv,Jianguang Yuan,Bao Zhang,Ying Wu
DOI: https://doi.org/10.1016/j.jallcom.2017.09.300
IF: 6.2
2017-01-01
Journal of Alloys and Compounds
Abstract:Structural and electrochemical performances of La0.75-xCexMg0.25Ni3Co0.5 (x = 0, 0.05, 0.1, 0.15, 0.2 at.%) alloys prepared by an induction melting under helium atmosphere followed by annealing treatment at 1173 K in a vacuum furnace for 8 h are studied. Rietveld refinement results from the XRD data suggest that the alloys are mainly composed of (La, Mg)Ni-3, (La, Mg)(2)Ni-7 and LaNi5 phases. Increasing the content of Ce, the amounts of (La, Mg)Ni-3 phase and (La, Mg)(2)Ni-7 phase decrease, while the amount of LaNi5 phase increases. Electrochemical performance measurement results show that the La0.75-xCexMg0.25Ni3Co0.5 alloys are completely activated within 2 cycles, and the cyclic stability after 100 charge/discharge cycles of the alloys increases from 62.39% to 84.94% with the rising of Ce content, and the discharge capacity of the 100th cycle reaches the maximum value of 259 mAh/g when Ce content is 0.1 at.%. Meanwhile, the high rate discharge ability of the alloy electrodes increases to the maximum value when Ce content is 0.1 at.%, and then decreases. Thus, the La0.75-xCexMg0.25Ni3Co0.5 alloy exhibits optimum comprehensive electrochemical properties. (C) 2017 Elsevier B.V. All rights reserved.