Abstract:The synthesis of ZnWO4 nanocrystals via hydrothermal reaction was systematically studied in the wide ranges of solution pH (2-11), temperature (up to 180 °C) and reaction duration (up to 24 h), and the course and mechanism of phase/morphology evolution were revealed. With the well-developed ZnWO4 nanorod powder (aspect ratio ∼7–20) as a representative, the effects of subsequent calcination (700 °C, in air and oxygen) on photoluminescent and photocatalytic performances were comparatively analyzed. Detailed characterization of the products was conducted by XRD, FE-SEM, HR-TEM, and FT-IR, Raman, fluorescence and UV–Vis spectroscopies. It was shown that the as-synthesized and calcined ZnWO4 crystallites all exhibited broad excitation (∼225–325 nm, peaked at ∼283 nm; λem = 482 nm) and emission (∼400–700 nm, maxima at ∼ 482 nm; λex = 283 nm) that arise from the 1A1g → 1T1u and 3T1u → 1A1g electronic transitions within the WO6 ligand, respectively. Calcination in air and oxygen improved the integrated emission intensity by ∼1.54 and 1.65 times, respectively. The calcination, however, significantly deteriorated the photocatalytic capability of ZnWO4 toward the degradation of methyl orange (MO) under UV irradiation. It was shown that ∼93% of the MO molecules were degraded by the as-synthesized ZnWO4 nanorods with 80 min of UV radiation, while the values are only ∼39.1 and 44.4% for the powders calcined in air and oxygen, respectively. The above results were interpreted by considering interaction of the excited electrons with oxygen vacancy defects, electron-hole interaction and UV absorbance of the ZnWO4 products.

Microwave-Hydrothermal Synthesis and Photocatalytic Properties of Ag+ Doped ZnWO4 Nanorods

Microwave Hydrothermal Synthesis and Photocatalytic Properties of ZnWO4 Nanorods

Effect of ammonia on morphology, wettability and photoresponse of ZnO nanorods grown by hydrothermal method

The Microwave-Hydrothermal Synthesis and Photocatalytic Properties of ZnWO4 Nanowires

Synthesis, Characterization and Optical Properties of Nanostructured ZnWO 4

A Facile Microwave-Hydrothermal Method to Fabricate B Doped Znwo4 Nanorods with High Crystalline and Highly Efficient Photocatalytic Activity

Photoluminescent and photocatalytic ZnWO4 nanorods via controlled hydrothermal reaction

Hydrothermal Synthesis and Photocatalytic Activity of Zinc Oxide Nanorods

Template-free Hydrothermal Synthesis and High Photocatalytic Activity of ZnWO4 Nanorods

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Rapid Synthesis of Zn2+ Doped Snwo4 Nanowires with the Aim of Exploring Doping Effects on Highly Enhanced Visible Photocatalytic Activities

Synthesis and Photocatalytic Properties of Ag /zns Core /shell Nanorods

Synthesis of Mo-doped ZnWO<sub>4</sub> Nanoparticles with Enhanced Photocatalytic Properties

Microwave Hydrothermal Synthesis of Cr~(3+)-doped ZnO Nanoparticles and Their Photocatalytic Properties

Hydrothermal Preparation and Photoluminescence Property of Co-Doped ZnO Nanorods

Synthesis of Ag/Zno Nanorods Array with Enhanced Photocatalytic Performance

Controlled Hydrothermal Synthesis of ZnO Nano and Microstructure Materials with Photocatalytic Properties

Particle Size and Structural Control of ZnWO4 Nanocrystals Via Sn2+ Doping for Tunable Optical and Visible Photocatalytic Properties

Synthesis of ZnWO4 nanorods with [100] orientation and enhanced photocatalytic properties

Controlled Synthesis Of The Znwo4 Nanostructure And Effects On The Photocatalytic Performance

Synthesis of ZnO Nanorods and Nanorod Arrays Through Hydrothermal Methods