Abstract:The synthesis of ZnWO4 nanocrystals via hydrothermal reaction was systematically studied in the wide ranges of solution pH (2-11), temperature (up to 180 °C) and reaction duration (up to 24 h), and the course and mechanism of phase/morphology evolution were revealed. With the well-developed ZnWO4 nanorod powder (aspect ratio ∼7–20) as a representative, the effects of subsequent calcination (700 °C, in air and oxygen) on photoluminescent and photocatalytic performances were comparatively analyzed. Detailed characterization of the products was conducted by XRD, FE-SEM, HR-TEM, and FT-IR, Raman, fluorescence and UV–Vis spectroscopies. It was shown that the as-synthesized and calcined ZnWO4 crystallites all exhibited broad excitation (∼225–325 nm, peaked at ∼283 nm; λem = 482 nm) and emission (∼400–700 nm, maxima at ∼ 482 nm; λex = 283 nm) that arise from the 1A1g → 1T1u and 3T1u → 1A1g electronic transitions within the WO6 ligand, respectively. Calcination in air and oxygen improved the integrated emission intensity by ∼1.54 and 1.65 times, respectively. The calcination, however, significantly deteriorated the photocatalytic capability of ZnWO4 toward the degradation of methyl orange (MO) under UV irradiation. It was shown that ∼93% of the MO molecules were degraded by the as-synthesized ZnWO4 nanorods with 80 min of UV radiation, while the values are only ∼39.1 and 44.4% for the powders calcined in air and oxygen, respectively. The above results were interpreted by considering interaction of the excited electrons with oxygen vacancy defects, electron-hole interaction and UV absorbance of the ZnWO4 products.

Microwave Hydrothermal Synthesis and Photocatalytic Properties of ZnWO4 Nanorods

Microwave-Hydrothermal Synthesis and Photocatalytic Properties of Ag+ Doped ZnWO4 Nanorods

The Microwave-Hydrothermal Synthesis and Photocatalytic Properties of ZnWO4 Nanowires

A Facile Microwave-Hydrothermal Method to Fabricate B Doped Znwo4 Nanorods with High Crystalline and Highly Efficient Photocatalytic Activity

Photoluminescent and photocatalytic ZnWO4 nanorods via controlled hydrothermal reaction

Synthesis, Characterization and Optical Properties of Nanostructured ZnWO 4

Template-free Hydrothermal Synthesis and High Photocatalytic Activity of ZnWO4 Nanorods

Controlled Synthesis Of The Znwo4 Nanostructure And Effects On The Photocatalytic Performance

Particle Size and Structural Control of ZnWO4 Nanocrystals Via Sn2+ Doping for Tunable Optical and Visible Photocatalytic Properties

Rapid Synthesis of Zn2+ Doped Snwo4 Nanowires with the Aim of Exploring Doping Effects on Highly Enhanced Visible Photocatalytic Activities

Hydrothermal Synthesis and Characterization of CdWO4 Nanorods

Synthesis of ZnWO4 nanorods with [100] orientation and enhanced photocatalytic properties

Hydrothermal Synthesis and Photocatalytic Activity of Zinc Oxide Nanorods

Synthesis Of Cdwo4 Nanorods And Investigation Of The Photocatalytic Activity

Microwave Hydrothermal Synthesis of Cr~(3+)-doped ZnO Nanoparticles and Their Photocatalytic Properties

Hydrothermal Preparation and Photoluminescence Property of Co-Doped ZnO Nanorods

Controlled Hydrothermal Synthesis of ZnO Nano and Microstructure Materials with Photocatalytic Properties

Microwave-assisted hydrothermal synthesis and characterization of hierarchical structured ZnO nanorods

Microstructure and Photoluminescence of Zno:Cd Nanorods Synthesized by Hydrothermal Method

Fabrication and Photocatalysis of Rod-Like Znwo4 Nanocrystallites

Synthesis of Mo-doped ZnWO<sub>4</sub> Nanoparticles with Enhanced Photocatalytic Properties