Spectroscopic Analysis of Er:Y2O3 Crystal at 2.7 Μm Mid-Ir Laser

Wentao Hou,Zian Xu,Hengyu Zhao,Yanyan Xue,Qingguo Wang,Xiaodong Xu,Jun Xu
DOI: https://doi.org/10.1016/j.optmat.2020.110017
IF: 3.754
2020-01-01
Optical Materials
Abstract:High quality 7 at%Er:Y2O3 crystal was successfully grown by Fz method. Judd-Ofelt theory was applied to analyze spectroscopic properties at 2.7 mu m. The larger value of Omega(2) shows low local environment symmetry exists in Er:Y2O3 crystal, and the large Omega(4)/Omega(6) indicates better spectral quality. The larger absorption cross-section and FWHM are beneficial to efficient absorption of pump source. The fluorescence spectra and lifetimes of Er:Y2O3 crystal were measured and studied at 2.7 mu m. The emission cross-sections at 2723 nm was calculated to be 1.41 x 10(-20)cm(2). Compared with other Er3+ doped crystals, the large spectral quality factors Q and low fluorescence lifetime ratio illustrate that Er:Y2O3 crystal has excellent laser properties at 2.7 mu m. In addition, the low inversion ratio also indicates great potential of Er:Y2O3 crystal for laser generation at 2.7 mu m.
What problem does this paper attempt to address?