Incorporation of Al2O3, GO, and Al2O3@GO nanoparticles into water-borne epoxy coatings: abrasion and corrosion resistance
Jia-qi Huang,Kunming Liu,Xinlong Song,Guocheng Zheng,Qing Chen,Jiadi Sun,Haozhe Jin,Lanlan Jiang,Yusheng Jiang,Yi Zhang,Peng Jiang,Wangping Wu
DOI: https://doi.org/10.1039/d2ra04223a
IF: 4.036
2022-01-01
RSC Advances
Abstract:Nano-Al2O3 particles and graphene oxide (GO) nanosheets were modified by 3-aminopropyltriethoxysilane (KH550), and then dispersed in epoxy resin, and finally modified-Al2O3/epoxy, modified-GO/epoxy and modified-Al2O3@GO/epoxy composite coatings were prepared on steel sheets by the scraping stick method. The microstructure, phase identification, surface bonding and composition of the nanoparticles were characterized by SEM, XRD, FT-IR, and Raman spectroscopy, respectively. The hardness of the coating was assessed by the pencil hardness method. The abrasion resistance of the coating was tested by a sand washing machine. The corrosion resistance of the coating was assessed using salt spray, a long-period immersion test, potentiodynamic polarization curves and electrochemical impedance spectra. With the addition of a small amount of nanoparticles, the dispersion of nanoparticles in the epoxy resin was good. When the content of nano-Al2O3 particles was equal to 1.5 wt%, the particles in the epoxy exhibited the best dispersion and stability. However, the GO and Al2O3@GO nanofillers in the epoxy resin exhibited poor dispersion and stability. The hardness, abrasion and corrosion resistance of the composite coatings were improved with the addition of a small amount of nanoparticles, but the performance began to decline after exceeding a certain content range of the nanoparticles. A relatively good abrasion resistance for the coatings was obtained when the content of Al2O3, GO and Al2O3@GO after modification was 1.5 wt%, 0.2 wt% and 0.4 wt%, respectively. The corrosion resistance of the coatings doped with nano-Al2O3 particles was better than that of the coatings incorporating GO nanosheets and Al2O3@GO hybrids. The corrosion mechanism of the composite coatings in 3.5 wt% NaCl solution was addressed and studied.