Abstract:Three types of inorganic fillers - fumed nonporous nano-silica, synthesized mesoporous MCM-41 and microporous zeolite 4A, were incorporated into the PVDF matrix to prepare mixed matrix membranes. The objective of this study was to investigate the effects of pore structure and particle size of the inorganic fillers on the gas transport properties of the mixed matrix membranes. The membranes were characterized using thermogravimetric analysis (TGA), differential scanning calorimetry (DSC). X-ray diffraction (XRD), contact angle tests and scanning electron microscopy (SEM). The mechanical properties of the membranes were determined using a tensile stress-strain machine. With the incorporation of the inorganic fillers, the thermal stability of the composite membranes was reduced with lower degradation temperature while the melting temperature and crystallizing temperature seemed to be unaffected. The DSC results showed that the crystallinity of the composite membranes had increased when compared with the pure PVDF membrane. In addition, the incorporation of MCM-41 had induced PVDF crystalline phase transformation from alpha to beta phase. This phenomenon was not observed in PVDF/SiO2 and PVDF/4A composite membranes as indicated by the XRD results. In order to fully study the interface properties between the inorganic fillers and polymer chains, the density values of the membranes were experimentally determined and compared with the theoretical values. The experimentally determined density values of the composite membranes were lower than the theoretical values and the void volume fractions were calculated accordingly. The single gas (He, CO2, O-2 and N-2) permeabilities of the resulting membranes were carried out. The gas permeabilities of the three composite membranes exhibited similar behaviors, especially at lower inorganic filler loadings, although the inorganic fillers had different pore structures and particle sizes. The highest permeabilities for CO2 and O-2 were obtained by PVDF/4A 32% composite membrane, which were 3.26 and 0.41 Barrer, respectively, and the highest permeabilities for He and N2 were obtained by PVDF/MCM-41 32% composite membrane, which were 10.2 and 0.14 Barrer, respectively. These permeabilities are much higher than those of pure PVDF membrane. The highest selectivities of 120.7, 33.1 and 4.6 for He/N-2, CO2/N-2, and O-2/N-2, were obtained by the PVDF/SiO2 4%, PVDF/SiO2 32% and PVDF/SiO2 24%, respectively, which are also higher than those of pure PVDF membrane. (C) 2012 Elsevier B.V. All rights reserved.

Fabrication of Mixed Matrix Membranes with Zinc Ion Loaded Titanium Dioxide for Improved CO2 Separation

Mixed Matrix Membranes for C2H4/C2H6 Separation Using a Phosphate Anion-Pillared Microporous Material

Enhanced CO2 Selectivity of Mixed Matrix Membranes with Carbonized Zn/Co Zeolitic Imidazolate Frameworks

Preparation and Characterization of Mixed Matrix Membranes Based on PVDF and Three Inorganic Fillers (fumed Nonporous Silica, Zeolite 4A and Mesoporous MCM-41) for Gas Separation

Mixed Matrix Membrane Based on Cross-Linked Poly[(ethylene glycol) methacrylate] and Metal–Organic Framework for Efficient Separation of Carbon Dioxide and Methane

Study On Co2 Facilitated Separation Of Mixed Matrix Membranes Containing Surface Modified Mwcnts

Mixed Matrix Membranes Incorporating Amino-Functionalized ZIF-8-NH2 in a Carboxylic Polyimide for Molecularly Selective Gas Separation

Poly(1-Trimethylsilyl-1-Propyne)-Based Hybrid Membranes: Effects Of Various Nanofillers And Feed Gas Humidity On Co2 Permeation

Carbon Nanotubes Grown on ZIF-L(Zn@Co) Surface Improved CO2 Permeability of Mixed Matrix Membranes

Mixed Matrix Membranes Based on Nanoparticle, Nanorod, and Nanosheet MFI-Type Zeolites for Gas Separation

Thermally Annealed High-Aspect-Ratio ZIF-8 Nanoplates-Incorporated Mixed Matrix Membranes for Improved H2/CO2 Selectivity

Thin Film Mixed Matrix Hollow Fiber Membrane Fabricated by Incorporation of Amine Functionalized Metal-Organic Framework for CO2/N2 Separation

Improving the Selectivity of ZIF-8/Polysulfone-Mixed Matrix Membranes by Polydopamine Modification for H2/CO2 Separation

Morphologically Tunable MOF Nanosheets in Mixed Matrix Membranes for CO2 Separation

Asymmetric Polyimide Mixed Matrix Membranes with Porous Materials-Modified Surfaces for CO2/N2 and CO2/CH4 Separations

Enhancement of CO2 separation efficiency in mixed matrix membranes through zinc ion modified g‐C3N4 nanosheets

Carbon nanotubes grown on ZIF-L(Zn@Co) surface improved CO 2 permeability of mixed matrix membranes

Modification of CO2-selective mixed matrix membranes by a binary composition of poly(ethylene glycol)/NaY zeolite

Preparation and Characterization of Mixed Matrix Membranes Based on Poly(vinylidene Fluoride) and Zeolite 4A for Gas Separation

Controlled Covalent Functionalization of ZIF-90 for Selective CO2 Capture & Separation

Phenolic resin regulated interface of ZIF-8 based mixed matrix membrane for enhanced gas separation