Facile synthesis and gas-sensing properties of monodisperse alpha-Fe2O3 discoid crystals

Peng Sun,Yingwei Liu,Xiaowei Li,Yanfeng Sun,Xishuang Liang,Fengmin Liu,Geyu Lu
DOI: https://doi.org/10.1039/c2ra21445h
IF: 4.036
2012-01-01
RSC Advances
Abstract:Monodisperse alpha-Fe2O3 discoid crystals have been prepared through a hexamethylenetetramine (HMT)-assisted hydrothermal process combined with subsequent acid-dissolution. First, uniform alpha-Fe2O3 round-edged hexahedrons with a size of about 1.2 mu m were synthesized. Subsequently, by a controlled acid etching process, the as-obtained alpha-Fe2O3 uniform hexahedrons could be facilely transformed into monodisperse alpha-Fe2O3 discoid crystals, without influencing the original crystal phase. Both field emission scanning electron microscope results and transmission electron microscope results revealed that the "discuses" were made of piled up nanoparticles. The selected area electron diffraction pattern from the whole discoid crystal displayed that all the nanoparticles were highly oriented, which resulted in the single-crystal "discus" features. To demonstrate the usage of such alpha-Fe2O3 discoid crystals, the obtained sample was applied to fabricate a gas sensor which was then tested for sensitivity to three kinds of gases (ethanol, methanol and acetone). The results of the test showed that the sensor had a high level of response and good recovery characteristics towards ethanol at the operating temperature of 238 degrees C.
What problem does this paper attempt to address?