Electrospun carbon nanofiber inlaid with tungsten carbide nanoparticle by in-situ carbothermal reaction as bifunctional electrode for vanadium redox flow battery

Gang Cheng,Yingqiao Jiang,Yuehua Li,Jian Chen,Zhangxing He,Wei Meng,Lei Dai,Ling Wang
DOI: https://doi.org/10.1016/j.electacta.2020.137178
IF: 6.6
2020-01-01
Electrochimica Acta
Abstract:This work provided a novel tungsten carbide (WC) nanoparticle catalyst which was uniformly inlaid in carbon nanofiber (CNF) without help of binder by in-situ carbothermal reaction and electrospinning technology to obtain CNF/WC composite for use as bifunctional electrode for vanadium redox flow battery (VRFB). Ammonium tungstate was used as tungstate source to obtain CNF/WC composites consisting of different amounts of WC (CNF/WC-05, CNF/WC-10, and CNF/WC-20). Ammonium tungstate was decomposed to tungsten trioxide at high temperature, which was subsequently converted to WC by way of an in-situ carbothermal reaction with increasing temperature. The electrochemical performance of CNF/WC composite is improved due to that WC nanoparticle can increase active sites towards vanadium redox reaction. CNF/WC-10 presents the best electrochemical performance for V3+/V2+ redox reaction as well as an increase in electrochemical performance for VO2+/VO2+ redox reaction compared with CNF. The cell using CNF/WC-10 as bifunctional electrode exhibits an increase in energy storage performance including higher energy efficiency and discharge capacity. In comparison with pristine cell, the cell using CNF/WC-10 shows better stability in 50-cycle charge-discharge operation at 50 mA cm−2. Especially, the cell using CNF/WC-10 presents an increase in energy and voltage efficiency compared with pristine cell at high current density, suggesting that CNF/WC-10 electrode decreases electrochemical polarization of cell. At 150 mA cm−2, the cell using CNF/WC-10 presents an increase of 7.2% in energy efficiency compared with pristine cell (61.1%). Overall, the results demonstrate excellent electrochemical performance of WC for vanadium redox reaction and provide guidelines for exploring carbide catalyst in future VRFB study.
What problem does this paper attempt to address?