Binder-Free CNT-Modified Excellent Electrodes for All-Vanadium Redox Flow Batteries

Nitika Devi,Prabhakar Singh,Yong-Song Chen
DOI: https://doi.org/10.3390/nano14090767
IF: 5.3
2024-04-26
Nanomaterials
Abstract:Electrodes are one of the key components that influence the performance of all-vanadium redox flow batteries (VRFBs). A porous graphite felt with modified fiber surfaces that can provide a high specific activation surface is preferred as the electrode of a VRFB. In this study, a simple binder-free approach is developed for preparing stable carbon nanotube modified graphite felt electrodes (CNT-GFs). Heat-treated graphite felt electrodes (H-GFs) are dip-coated using CNT homogeneous solution. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) results conclude that CNT-GFs have less resistance, better reaction currents, and reversibility as compared to H-GF. Cell performances showed that CNT-GFs significantly improve the performance of a VRFB, especially for the CNT-GF served in the positive side of the VRFB. CNT presence increases the electrochemical properties of the graphite electrode; as a result, reaction kinetics for both VO2+/VO2+ and V3+/V2+ are improved. Positive CNT-GF (P-CNT-GF) configured VRFB exhibits voltage efficiency, coulombic efficiency, and energy efficiency of 85%, 97%, and 82%, respectively, at the operating current density of 100 mA cm−2. At high current density of 200 mA cm−2, the VRFB with P-CNT-GF shows 73%, 98%, and 72% of the voltage, coulombic, and energy efficiencies, respectively. The energy efficiency of the CNT-GF is 6% higher when compared with that of B-H-GF. The VRFB with CNT-GF can provide stable performance for 300 cycles at 200 mA cm−2.
materials science, multidisciplinary,nanoscience & nanotechnology,physics, applied,chemistry
What problem does this paper attempt to address?
This paper aims to address the issue of poor electrode performance in vanadium redox flow batteries (VRFBs). Specifically, the researchers developed a simple and binder-free method to prepare carbon nanotube-modified graphite felt electrodes (CNT-GFs) to enhance the electrochemical performance of the electrodes. By uniformly coating carbon nanotubes (CNTs) on heat-treated graphite felt (H-GFs), the researchers found that this novel electrode exhibited lower resistance, better reaction current, and higher reversibility. Experimental results showed that at a working current density of 100 mA cm⁻², the VRFB configured with a positive CNT-GF exhibited 85% voltage efficiency, 97% coulombic efficiency, and 82% energy efficiency. Even at a higher current density of 200 mA cm⁻², the VRFB still achieved 73%, 98%, and 72% voltage, coulombic, and energy efficiencies, respectively. Compared to using only heat-treated graphite felt (H-GFs), CNT-GFs improved energy efficiency by 6%. Additionally, the VRFB maintained stable performance after 300 cycles at a current density of 200 mA cm⁻². Overall, this study provides an effective method for enhancing the performance of vanadium redox flow batteries.