Preparation and Characterization of Monodisperse Core-Shell Fe3O4@SiO2 Microspheres and Its Application for Magnetic Separation of Nucleic Acids from E. Coli BL21.
Chao Ma,Chuanyan Li,Nongyue He,Fang Wang,Ningning Ma,Liming Zhang,Zhuoxuan Lu,Zeeshan Ali,Zhijiang Xi,Xiaolong Li,Gaofeng Liang,Hongna Liu,Yan Deng,Lijian Xu,Zhifei Wang
DOI: https://doi.org/10.1166/jbn.2012.1454
2012-01-01
Journal of Biomedical Nanotechnology
Abstract:In this article, we present an easy route to prepare monodisperse core-shell Fe3O4@SiO2 microspheres with uniform size and shape. Their structures and properties were studied by transmission electron microscopy (TEM), scanning electron microscopy (SEM), Fourier transform infrared spectrometry (FT-IR), and vibrating sample magnetometer (VSM), respectively. The results showed that spherical Fe3O4 microspheres with well dispersion have a rough surface and an average diameter (about 500 nm). After the modification with silica, the particles have a well-defined core-shell structure and a much smoother surface and larger particle diameter (about 600 nm). Furthermore, VSM measurements indicated that the as-prepared Fe3O4 and Fe3O4@SiO2 microspheres were superparamagnetic at room temperature and the saturation magnetization (M(s)) were 58.110 emu/g and 33.479 emu/g, respectively. And then, the prepared monodisperse core-shell Fe3O4@SiO2 microspheres were subsequently applied to separate nucleic acids from the bacteria (E. coli BL21) and verified the great application prospects for bioseparation technology of the biomoleculars.