Preparation and Electromagnetic Wave-Absorbing Properties of Micro-Polyaniline/Fe3o4 Hollow Spheres
Li Tao,Zhang Long,Chen Ying,Guo Yajun,Du Xueyan
DOI: https://doi.org/10.7503/cjcu20141000
2015-01-01
Abstract:Doped polyaniline/Fe3O4(D-PANI/Fe3O4) with hollow spheres were prepared by the combination of interfacial polymerization and Pickering emulsion polymerization method with toluene as soft template, Fe3O4 nanoparticles as cosurfactant, sodium dodecyl benzene sulfonate(SDBS) as emulsifier, ammonium persulfate (APS) as oxidant, hydrochloric acid (HCl) as the doping agent. And as a comparison, the polyaniline/Fe3O4 (PANI/Fe3O4) with hollow spheres were prepared without acid doping. The morphology, structure, integrant, magnetic and electrical properties of the composite material were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), thermogravimetric (TG), vibration sample magnetism (VSM) and the four-probe method, respectively. The results indicate that the D-PANI/Fe3O4 with hollow spheres structures were prepared successfully. The diameter of D-PANI/Fe3O4 hollow spheres was about 2. 8 mu m, the conductivity and saturation magnetization (M-s) of D-PANI/Fe3O4 hollow spheres were 2. 75 x10(-2) S/cm and 54. 26A . m(2)/kg, respectively. The quality of Fe3O4 nanoparticles accounted for about 28% of D-PANI/Fe3O4 hollow spheres. Electromagnetic properties and wave absorption performance of D-PANI/Fe3O4 hollow spheres and PANI/Fe3O4 hollow spheres were analyzed by vector network analyzer (VNA). The results showed that the best absorbing property and minimum reflection loss (RL) of D-PANI/Fe3O4 composites were -43. 3 dB at 12. 64 GHz with the matching thickness of 2 mm, and the wave absorption performance was superior to PANI/Fe3O4 composites.