Influence of MnOx Loading on Activity of MnOx/Ce0.7Zr0.2La0.1O2-Al2O3 Catalyst for Catalytic Combustion of Diesel Soot

Zhu Yi,Pan Hao,Chen Shanhu,Wang Shidan,Zhao Ming,Gong Maochu,Chen Yaoqiang

DOI: https://doi.org/10.3724/sp.j.1088.2012.20746

2013-01-01

CHINESE JOURNAL OF CATALYSIS (CHINESE VERSION)

Abstract:A series of MnOx/Ce0.7Zr0.2La0.1O2-Al2O3 supported catalysts with the Ce0.7Zr0.2La0.1O2:Al2O3 mass ratio of 1:1 and different MnOx loadings were prepared by the incipient wetness method. The catalysts were characterized by X-ray diffraction, low temperature N-2 adsorption-desorption, X-ray photoelectron spectroscopy, O-2 temperature-programmed desorption, and H-2 temperature-programmed reduction. The catalytic performance of these catalysts for the combustion of diesel soot was investigated. It is found that surface-adsorbed active oxygen species and low-temperature reducibility of MnOx are the determinants of catalytic activity. When the MnOx loading is 5%, the catalyst activity decreases owing to the loss of active oxygen species, which are necessary for the catalytic combustion. When the MnOx loading is increased to 10%, the catalyst activity is dramatically increased because of the enhanced reducible manganese species. Interestingly, the optimal values for reducible manganese species and surface-adsorbed oxygen species can be achieved in the catalyst with 20% MnOx and so the catalyst exhibits the best catalytic activity, giving a light-off temperature about 179 degrees C lower than that of the non-catalytic soot combustion. With a further addition of MnOx species up to 30%, its catalytic activity is deteriorated mainly due to the decrease in surface-trapped oxygen species and upper shift of the reduction temperature.