Abstract:The recent report of pressure-induced structural transition and signature of superconductivity with T c ≈ 80 K above 14 GPa in La 3 Ni 2 O 7 crystals has garnered considerable attention. To further elaborate this discovery, we carried out comprehensive resistance measurements on La 3 Ni 2 O 7 crystals grown in an optical-image floating zone furnace under oxygen pressure (15 bar) using a diamond anvil cell (DAC) and cubic anvil cell (CAC), which employ a solid (KBr) and liquid (glycerol) pressure-transmitting medium, respectively. Sample 1 measured in the DAC exhibits a semiconducting-like behavior with large resistance at low pressures and gradually becomes metallic upon compression. At pressures P ⩾ 13.7 GPa we observed the appearance of a resistance drop of as much as ∼ 50% around 70 K, which evolves into a kink-like anomaly at pressures above 40 GPa and shifts to lower temperatures gradually with increasing magnetic field. These observations are consistent with the recent report mentioned above. On the other hand, sample 2 measured in the CAC retains metallic behavior in the investigated pressure range up to 15 GPa. The hump-like anomaly in resistance around ∼ 130 K at ambient pressure disappears at P ⩾ 2 GPa. In the pressure range of 11–15 GPa we observed the gradual development of a shoulder-like anomaly in resistance at low temperatures, which evolves into a pronounced drop of resistance of 98% below 62 K at 15 GPa, reaching a temperature-independent resistance of 20 μΩ below 20 K. Similarly, this resistance anomaly can be progressively shifted to lower temperatures by applying external magnetic fields, resembling a typical superconducting transition. Measurements on sample 3 in the CAC reproduce the resistance drop at pressures above 10 GPa and realize zero resistance below 10 K at 15 GPa even though an unusual semiconducting-like behavior is retained in the normal state. Based on these results, we constructed a dome-shaped superconducting phase diagram and discuss some issues regarding the sample-dependent behaviors on pressure-induced high-temperature superconductivity in the La 3 Ni 2 O 7 crystals.

Study of the Pressure−Time−Temperature Transformation of Amorphous La6Ni5Al89 by the Energy Dispersive Method for Phase Transition

First-principles Investigation of the Concentration-Dependent Phase Transition of Alloys

Low Temperature X-Ray Diffraction Study On Phase Transitions

Pressure Effects on Al89La6Ni5 Amorphous Alloy Crystallization

Influence of W, Mo and Ti trace elements on the phase separation in Al8Co17Cr17Cu8Fe17Ni33 based high entropy alloy

In Situ Phase Transition Study of Nano- and Coarse-Grained Tio(2) under High Pressure/Temperature Conditions

Evidence of Eutectic Crystallization and Transient Nucleation in Al89La6Ni5 Amorphous Alloy

Evidence for a phase transition in an AlCrFe2Ni2 high entropy alloy processed by high-pressure torsion

Temperature- and Pressure-Induced Polyamorphic Transitions in AuCuSi Alloy

Phase Equilibria in the Al–Co–Cr–Fe–Ni High Entropy Alloy System: Thermodynamic Description and Experimental Study

Emergence of High-Temperature Superconducting Phase in Pressurized La3Ni2O7 Crystals

Phase stability of a eutectic high entropy alloy under extremes of pressures and temperatures

IDENTIFYING THE GLASS TRANSITIONS IN Al85Ni5Y6-Fe2Co2 METALLIC GLASS USING TEMPERATURE MODU-LATED DIFFERENTIAL SCANNING CALORIMETRY

Origin of pressure-induced crystallization of Ce75Al25 metallic glass.

Crystallization and phase separations in amorphous Cu12.5Ni10Zr41Ti14Be22.5 alloy, as investigated by sans

Emergence of high-temperature superconducting phase in the pressurized La3Ni2O7 crystals

Debye temperature, electron-phonon coupling constant, and three-dome shape of crystalline strain as a function of pressure in highly compressed La$_3$Ni$_2$O$_{7-δ}$

High-temperature stability of chemically architectured high entropy alloys studied by X-ray diffraction and diffusion modelling

Structural Stability of Pd40Cu30Ni10P20 Metallic Glass in Supercooled Liquid Region

Lattice Distortion-Induced Sluggish Phase Transition in CoCrFeNixAl1-x (x =0.5, 0.75) High-Entropy Alloys at High Pressures

Structure and phase transformations of amorphous-nanocrystalline Al-based alloy