Novel triphenylamine polyamides bearing carbazole and aniline substituents for multi-colored electrochromic applications
Yu Liu,Tingjun Liu,Lifei Pang,Jinyu Guo,Jiuyang Wang,Duo Qi,Wenze Li,Kunzhi Shen
DOI: https://doi.org/10.1016/j.dyepig.2019.107995
IF: 5.122
2020-02-01
Dyes and Pigments
Abstract:A novel carbazolyl-derived diamine containing triphenylamine, 4,4′-bis[(4-aminophenyl)amino]-4″-carbazolyltriphenylamine (VI), was prepared via the reduction of 4,4′-bis[(4-nitrophenyl)amino]-4″-carbazolyltriphenylamine. A series of novel polyamides (PAs, individually denoted as VIIIA-VIIID) bearing carbazole-substituted triphenylamine units were subsequently prepared by direct polymerization of a novel diamine monomer (VI) and various aromatic diacids (VIIA-VIID). Cyclic voltammetry of the PAs cast onto an indium tin oxide (ITO) coated glass substrates revealed two reversible redox couples at 0.36–0.90 and 1.46–1.70 V under anodic scanning. Characterization of PA-VIIID showed that the resulting radical cations had excellent electrochromic properties, with their color changing from light yellow to green upon oxidation, and finally to dark blue in their fully oxidized form. Further, the optical contrast at 424 nm was 58.7%, while that at 820 nm was 74.2%. The coloring time at the specified wavelength of 424 nm was 3.4 s (during the oxidation process), the fading time was 3.9 s (during the reduction process), the coloring time at the specified wavelength of 820 nm was 3.9 s (during the oxidation process), and the fading time was 3.9 s (during the reduction process). In addition, the anodic coloring of the PA-VIIID showed a high coloring efficiency (CE = 203 cm2/C), and the long-term redox reversibility was measured according to the difference in the percentage of transmittance exhibited by PA-VIIID between 0.00 and 1.70 V.
engineering, chemical,chemistry, applied,materials science, textiles