Atomic Force Microscopic Investigation on Surface Structure Related to Growth Kinetics on (101) Face of Potassium Dihydrogen Phosphate and Potassium Dideuterium Phosphate (D=99.8%) Crystals

Jianxu Ding,Shenglai Wang,Yijie Gu,Guogang Xu,Hongquan Liu,Yanmin Wang

DOI: https://doi.org/10.1166/nnl.2014.1839

2014-01-01

Nanoscience and Nanotechnology Letters

Abstract:The surface structure on (101) faces of both potassium dihydrogen phosphate (KDP) and potassium dideuterium phosphate (DKDP, D = 99.8%) crystals at various supersaturations were comparatively investigated by using atomic force microscope (AFM). The results revealed that the elemental steps on (101) face for both KDP and DKDP crystals whose step height was about the interplanar distance along [101] directions, could not be bunched together, which meant the step height maintained stable with a rise of supersaturation. However, the growth kinetic related parameter, slope of the steps, was increased with a rise of supersaturation, which was attributed to that the anionic growth units H2PO4- and D2PO4- were prone to be located onto the frontier of the step to narrow the terrace width. Additionally, owing to the dissimilarity of physico-chemical properties of D2PO4- to H2PO4-, such as the lower bond enthalpy of D-O bonds in D2PO4- than that of H-O bonds in H2PO4-, the supersaturation at the growth boundary layer for DKDP crystal was relative lower, which consequently resulted in lower slope of step compared with that for KDP crystal.