Abstract:The purposes of this study are to reduce Fe2O3 using hydrogen (H2) and carbon monoxide (CO) gases at a high temperature zone (500 °C–900 °C) by focusing on the influence of reduction gas concentrations. Reduction behavior of hematite (Fe2O3) at high temperature was examined using temperature programmed reduction (TPR) under non-isothermal conditions with the presence of 10% H2/N2, 20% H2/N2, 10% CO/N2, 20% CO/N2 and 40% CO/N2. The TPRCO results indicated that the first and second reduction peaks of Fe2O3 at a temperature below 660 °C appeared rapidly when compared to TPRH2. However, TPRH2 exhibited a better reduction in which Fe2O3 entirely reduced to Fe at temperature 800 °C (20% H2) without any remaining of wustite (FeO) whereas a temperature above 900 °C is needed for a complete reduction in 10% H2/N2, 10% and 20% CO/N2. Furthermore, the reduction of hematite could be improved when increasing CO and H2 concentrations since reduction profiles were shifted to a lower temperature. Thermodynamic calculation has shown that enthalpy change of reaction (ΔHr) for all phases transformation in CO atmosphere is significantly lower than in H2. This disclosed that CO is the best reductant as it is a more exothermic, more spontaneous reaction and able to initiate the reduction at a much lower temperature than H2 atmosphere. Nevertheless, the reduction of hematite using CO completed at a temperature slightly higher compared to H2. It is due to the presence of an additional carburization reaction which is a phase transformation of wustite to iron carbide (FeO → Fe3C). Carburization started at the end of the second stage reduction at 600 °C and 630 °C under 20% and 40% CO, respectively. Therefore, reduction by CO encouraged the formation of carbide, slower the reduction and completed at high temperature. XRD analysis disclosed the formation of austenite during the final stage of a reduction under further exposure with high CO concentration. Overall, less energy consumption needed during the first and second stages of reduction by CO, the formation of iron carbide and austenite were enhanced with the presence of higher CO concentration. Meanwhile, H2 has stimulated the formation of pure metallic iron (Fe), completed the reduction faster, considered as the strongest reducing agent than CO and these are effective at a higher temperature. Proposed iron phase transformation under different reducing agent concentrations are as followed: (a) 10% H2, 20% H2 and 10% C; Fe2O3 → Fe3O4 → FeO → Fe, (b) 20% CO; Fe2O3 → Fe3O4 → FeO → Fe3C → Fe and (c) 40% CO; Fe2O3 → Fe3O4 → FeO → Fe3C → Fe → F,C (austenite).

Effect of Carbon Coating on Magnetite Reduction

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Comparison of Microstructures of Magnetite Reduced by H2 and CO under Microwave Field

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

Effect of magnetite addition to ilmenite on hydrogen-rich reduction of its oxidized powder

Experimental Study on Strengthening Carbothermic Reduction of Vanadium-Titanium-Magnetite by Adding CaF2

Study on the reduction of Fe2O3 pellets by CO-CO2 and H2-H2O: Reaction kinetics and pore network model

Effect of MgO and CaCO3 As Additives on the Reduction Roasting and Magnetic Separation of Beach Titanomagnetite Concentrate

Influence of hydrogen and carbon monoxide on reduction behavior of iron oxide at high temperature: Effect on reduction gas concentrations

Characteristic and Mechanistic Study of Enhanced Carbon-Based Synfuel from Biomass and Coal by Magnetite Additive for Synergistic Co-Carbonization Technology.

Reduction kinetics of iron oxide pellets with H2 and CO mixtures

Investigation of Reducing Magnetite in Copper Slag Using CO–CO2

Pre-reduction of carbon-containing pellets of high chromium vanadium–titanium magnetite at different temperatures

High-Temperature Interactions Between Vanadium-Titanium Magnetite Carbon Composite Hot Briquettes and Pellets Under Simulated Blast Furnace Conditions

Wetting and Spreading Behavior of Molten Iron in Contact with Graphite Substrate: Interfacial Effects

Effect of Carbon Addition on Direct Reduction Behavior of Low Quality Magnetite Ore by Reducing Gas Atmosphere

Mechanism of Sodium Carbonate-Assisted Carbothermic Reduction of Titanomagnetite Concentrate

1 Kinetic Studies on Gas-Based Reduction of 2 Vanadium Titano-Magnetite Pellet 3

Kinetic Studies on Gas-Based Reduction of Vanadium Titano-Magnetite Pellet

Kinetic analysis of iron ore powder reaction with hydrogen—carbon monoxide

Effect of FeO concentration in sinter iron ore on reduction behavior in a hydrogen-enriched blast furnace