Abstract:The daily and annual temperature differences in mid and high latitudes areas vary greatly, which leads to thermal fatigue deterioration of concrete. The deterioration of concrete properties can also be generated by the cyclic change of humidity in concrete. In the experiment, the thermal fatigue tests of concrete with two strength grades were carried out at the temperature difference of 20 °C, 30 °C, and 40 °C (the initial temperature is 20 °C) under the condition of constant ambient humidity. The macroscopic properties change of concrete such as compressive strength and splitting tensile strength were measured. The microstructure changes of concrete were determined by ultrasonic nondestructive testing technique and mercury intrusion test. The results indicated that thermal fatigue has obvious deterioration effect on concrete. With the increase of temperature difference and cycle number, the strength of concrete decreased dramatically and the decrease of C40 concrete was greater than that of C25 concrete. The splitting tensile strength was more sensitive to thermal fatigue than compressive strength. The ultrasonic wave velocity gradually decreased and the damage factor increased, indicating the internal crack defects of concrete increased. At the same temperature difference, the porosity, total pore volume, average pore diameter, medium pore diameter, and the most probable pore diameter of concrete increased gradually with the increase of the cycle number, while the total pore surface area decreased. The pore structure showed the characteristics of coarsening and the trend of deterioration. The porosity of C40 concrete was less than that of C25 concrete, but the relative change value of porosity was larger, which reveals the internal reason for the strength damage of concrete under thermal fatigue at the microscopic level.

RELATIONSHIP BETWEEN FATIGUE BEHAVIOR AND MICROSTRUCTURE

Flexural strength and fatigue properties of interfacial transition zone at the microscale

Fatigue Degradation Properties of Pcm-Concrete Interface

Fatigue Performance of Prefabricated Composite T‐beams under Cyclic Overloading: an Experimental Study

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Effect of thermal fatigue on mechanical properties and microstructure of concrete in constant ambient humidity

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Experimental Study on Some Factors Affecting Fracture Property of Concrete

Discrete Element Modeling and Electron Microscopy Investigation of Fatigue-Induced Microstructural Changes in Ultra-High-Performance Concrete

Shear Fatigue Behavior of Reinforced Concrete Beams Produced with Manufactured Sand As Alternatives for Natural Sand

Quantitative study on the influence of fly ash content, saturation degree and interface transition zone on the permeability of cement-based materials

Microscopic Characterization of Concrete Durability Using Nano-Indentation Tests

Fatigue Performance Analysis of Fine Aggregate Matrix Using a Newly Designed Experimental Strategy and Viscoelastic Continuum Damage Theory

The Hydraulic Interface Towards the Anti-Fatigue Performance of Fiber-Calcium Silicate Hydrate Composites under Cyclic Loading

Micromechanical analysis of interfacial transition zone in alkali-activated fly ash-slag concrete

Modifying fatigue performance of reactive powder concrete through adding pozzolanic nanofillers

Capillary Water Absorption and Micro Pore Connectivity of Concrete with Fractal Analysis

Experimental Study and Analytical Modeling on Fatigue Properties of Pervious Concrete Made with Natural and Recycled Aggregates

Microstructural Analysis of the Effects of Compaction on Fatigue Properties of Asphalt Mixtures

A review of the interfacial transition zones in concrete: Identification, physical characteristics, and mechanical properties