Abstract:In order to produce the electrolytic manganese from the absorption solution of flue gas desulfurization with pyrolusite pulp, the absorption solution should be pretreated to remove the Fe 2+ ion and the heavy metal impurities in the solution. The Fe 2+ in the absorption solution was oxidized to Fe 3+ at first by adding oxidant H 2O 2 into the solution, and then the pH value of the solution was adjusted to 5.5±0.5 by adding aqueous ammonia to precipitate the Fe(OH) 3 formed by oxidation of Fe 2+. After filtration, the ferric impurities were removed, and then the sulphidation agent (NH 4) 2S of 50 mL·L -1 was added into the filtrate to form the precipitable sulphides of the heavy metals. Filtrate the filtrate once more, the heavy metal impurities were removed and the filtrate of the second time, the purified absorption solution, was ready to be electrolyzed. The electrolysis was conducted in an electrolytic device equipped with an anode of Ag/Sb/Sn/Pb alloy, a cathode of 1Crl8Ni9Ti stainless steel and an ion permeable separator of polyester fabric. The effects of operating parameters on the electric current efficiency and cell voltage were investigated. The suitable electrolysis conditions were found as follows. The electric current density used is 390 A·m -2, the operating temperature is 35°C, the concentration of (NH 4) 2SO 4, SeO 2 and Mn 2+ in the electrolyte are 110 g·L -1, 0.04 g·L -1 and 18 g·L -1, respectively, and in the influent, the Mn 2+ concentration is 26 g·L -1 and the pH value is 8. After conducting the pretreatments as mentioned before and operating under above proposed conditions, the metal impurities influencing the production of electrolytic manganese in the absorption solution will be removed, and the electrolytic manganese produced can meet the standard of GB3418-82. This study discloses a novel recycling approach of utilizing the resource coming from the flue gas desulfurization with pyrolusite pulp.

Extraction of Iron and Manganese from Pyrolusite Absorption Residue by Ammonium Sulphate Roasting–Leaching Process

An Environmentally Friendly Approach for the Extraction and Recovery of Mn from Pyrolusite by Ammonium Sulfate Roasting‐water Leaching and Ammonium Carbonate Precipitation

Extraction of Manganese from Iron Rich Mno2 Ores Via Selective Sulfation Roasting with So2 Followed by Water Leaching

The Extraction of Valuable Metals and Phase Transformation and Formation Mechanism in Roasting-Water Leaching Process of Laterite with Ammonium Sulfate

Efficient Extraction of Manganese from Low-Grade Pyrolusite by a Sawdust Pyrolysis Reduction Roasting-Acid Leaching Process

Study on Separation of Manganese from Iron in High-Iron Pyrolusite Ore by Leaching with Simulated Flue Gas

Effective separation of Zn, Fe, and Mn from roasting-water leaching solution of blast-furnace dust using a precipitation-solvent extraction process

Recovery of Iron and Manganese from Iron-Bearing Manganese Residues by Multi-Step Roasting and Magnetic Separation

Separation of Manganese from Iron in the SO_2 Reductive Leaching Iron-Rich Pyrolusite Ore: Leaching Mechanism and Kinetics

Manganese Extraction by Sulfur-Based Reduction Roasting–acid Leaching from Low-Grade Manganese Oxide Ores

Separation of Manganese from Iron in the $$\hbox {SO}_{2}$$ SO 2 Reductive Leaching Iron-Rich Pyrolusite Ore: Leaching Mechanism and Kinetics

Extraction of nickel from ferromolybdenum leach residues

Novel Process of Reduction Roasting Manganese Ore with Sulfur Waste and Extraction of Mn by Acid Leaching

Study on the Process of Preparaing Electrolytic Manganese from Absorption Solution of Flue Gas Desulfurization with Pyrolusite Pulp

Novel Process For Utilizing Low-Grade Manganese Oxide Ores By Sulfur-Based Reduction Roasting-Acid Leaching

Reductive Roasting of Iron-Rich Manganese Oxide Ore with Elemental Sulfur for Selective Manganese Extraction

Manganese extraction from high-iron-content manganese oxide ores by selective reduction roasting-acid leaching process using black charcoal as reductant

Extraction and Separation of Mn and Pb from Electrolytic Manganese Anodic Slime (EMAS) Via SO2 Roasting Followed by Acid Leaching Process

A Process for Extraction of Manganese from Manganese Oxide Ores by a Novel and Efficient Roasting-Acid Leaching Technique

Iron Extraction from Red Mud using Roasting with Sodium Salt

Separation and Recovery of Iron and Manganese from High-Iron Manganese Oxide Ores by Reduction Roasting and Magnetic Separation Technique